为了提高涤纶织物数字印花效果,本研究采用TEMPO(2,2,6,6-四甲基哌啶-氮-氧化物)氧化法制备了氧化微纤化纤维素(T-MFC),结合助剂制备预处理液。采用数字喷墨方式,研究了T-MFC在预处理液中的用量变化对涂布后的涤纶织物数字印花性能的影响。结果表明:T-MFC在预处理液中占比0.7%(质量分数)为最优T-MFC预处理方案,与未处理织物相比,此时织物C、M、Y、K四色印花K/S值分别提升了29.1%、123.1%、51.0%、10.9%,墨点圆度C值从1.38降至1.25左右,印花文本质量得到改善。TEMPO氧化改性的T-MFC作为预处理液中的亲水剂,将其涂布在涤纶织物表面可以改善织物的亲水性,提高织物表面印花效果。
In order to improve the digital printing effect of polyester fabric,oxidized microfibrillated cellulose(TMFC)was prepared by using TEMPO(2,2,6,6-tetramethylpiperidine-nitrogen oxide)oxidation method,and the pretreatment solution was prepared by combining with the auxiliary agent.The influence of the amount of T-MFC in the pretreatment solution on the digital printing performance of the coated polyester fabric was studied by using digital inkjet method.The results showed that when the proportion of T-MFC in the pretreatment solution is 0.7wt%,T-MFC finishing is the best scheme.Compared with untreated fabrics,at this time,the K/S value of fabric printing C,M,Y and K is increase by 29.1%、123.1%、51.0%、10.9%.The C value of ink dot roundness decrease from 1.38 to 1.25.The quality of printed text has been improved.As a hydrophilic agent in pretreatment solution,TEMPO oxidized T-MFC is coated on the surface of polyester fabric to improve the hydrophilicity of the fabric and improve the printing effect on the surface of the fabric.
作者
姚晨筱
陈蕴智
张正健
赵恬
YAO Chen-xiao;CHEN Yun-zhi;ZHANG Zheng-jian;ZHAO Tian(China Light Industry Key Laboratory of Food Packaging Materials and Technology,Tianjin University of Science and Technology,Tianjin 300457,China)
出处
《数字印刷》
CAS
北大核心
2021年第4期140-146,163,共8页
Digital Printing
基金
天津市自然科学基金(No.18JCQNJC76800)
天津市教委科研计划(No.2018KJ096,No.2018KJ095)
天津市企业科技特派员项目(No.19JCTPJC55200)。
关键词
微纤化纤维素
涤纶织物
数字印花
Microfibrillated cellulose
Polyester fabric
Digital printing