摘要
对冷轧钢板生产中出现的表面缺陷进行了分类,主要分析了孔洞类、氧化铁皮压入类、边裂类、起皮类等缺陷的主要待征及产生的原因;明确了相关缺陷产生的影响因素,并提出了相应的预防措施。
Cold-rolled steel plate surface defects appeared during production were categorized, and the major characteristics and forming causes of holes, iron oxide press-in, edge cracking, peeling defects were mainly analyzed. The effect factors for forming defects were affirmed and some relevant preventive measures were proposed.
出处
《机械工程材料》
CAS
CSCD
北大核心
2012年第7期100-104,共5页
Materials For Mechanical Engineering
基金
河北省自然科学基金资助项目(E2009000791)
关键词
冷轧钢板
表面缺陷
孔洞
氧化铁皮压入
边裂
cold rolled steel plate
surface defect
hole
iron oxide press-ira edge cracking