摘要
通过浸泡失重率、水蒸气透过率、孔洞率、交流阻抗技术(EIS)和机械性能测试等方法,研究了玻璃鳞片在酚醛环氧乙烯基酯树脂防腐涂料中的作用。结果表明,在防腐涂料中C型玻璃鳞片具有良好的耐蚀性;同时在喷涂型涂料中,选择200目玻璃鳞片较好。在3.5%NaCl溶液中浸泡120d后,玻璃鳞片与酚醛环氧乙烯基酯树脂的质量比为30/100的涂层电阻仍然在109Ω.cm2以上,比未添加乙烯基酯树脂的涂层电阻高2个数量级,涂层电容稳定为8.40×10-11F/cm2左右。
By means of mass loss experiments, vapor permeation tests, hole percentage measurements, electrochemical impedance spectroscopy （EIS） and mechanical testing, it was shown that addition of 200-mesh C-type glass flakes led to improved corrosion resistance in sprayed coatings. It was found that the best corrosion and permeation resistance is obtained with a ratio of glass fiber to resin of 30：70. After immersion in a 3.5 % NaCl solution for 120 d, the resistance of the coating remained above 10^9Ω ·cm^2, two orders of magnitude larger than the resistance of a control coating without added glass flakes. During immersion, the value of the capacitance of the coating reached a limiting value around 8.40 × 10^-11 F/cm^2.
出处
《北京化工大学学报（自然科学版）》
EI
CAS
CSCD
北大核心
2007年第2期145-149,共5页
Journal of Beijing University of Chemical Technology(Natural Science Edition)
关键词
玻璃鳞片
乙烯基酯树脂
交流阻抗
耐蚀性
glass fiber
vinyl ester resin
electrochemical impedance spectroscopy （EIS）
anticorrosion