Silver has grown its attraction of the scientists in microelectronic field recently.Electrochemical deposition of silver onto copper substrates by immersion method has been one of the keen topics. In this study, ethan...Silver has grown its attraction of the scientists in microelectronic field recently.Electrochemical deposition of silver onto copper substrates by immersion method has been one of the keen topics. In this study, ethanol was used as the plating solution in which some chemicals were added. The silver deposits were characterized by a field emission scanning electron microscopy （FESEM）, an atom force microscope （AFM）, a transmission electron microscope （TEM） and a selected area electron diffraction （SAED）. It was found that silver immersion using ethanol-based bath has good coverage feature. The highlands of the copper substrate are coated by silver particles whose sizes are around 12 nm, but those sizes at low-lying lands are a little smaller.展开更多
Two kinds of silver based medium temperature brazing filler metals(45AgCuZnSn and 60AgCuSn) were selected to braze and seal brass flange pipe and copper pipe by high frequency heating brazing. In this paper, the quali...Two kinds of silver based medium temperature brazing filler metals(45AgCuZnSn and 60AgCuSn) were selected to braze and seal brass flange pipe and copper pipe by high frequency heating brazing. In this paper, the quality of the braze was evaluated by immersion ultrasound, and the microstructure of the brazed joint was observed by SEM and EDS. The experimental results show that the high frequency heating brazing can quickly achieve the device sealing;through the ultrasonic flaw detection image calculation, the brazed bonding rate obtained by 60AgCuSn brazing is 87%, and by 45AgCuZnSn brazing is 71%;the cross-sectional area of the brazed joint obtained by two kinds of silver based medium temperature brazing filler metals is observed, the brazed joint obtained by 45AgCuZnSn brazing has defects visual, and a large amount of Zn element gathered in the defects, there is no obvious porosity in the brazed joint by 60AgCuSn brazing,and the bonding layer is dense and coherent. Through the contrast test, the choice of 60AgCuSn alloy brazing can meet the needs of high frequency brazing of brass flange pipe and copper pipe.展开更多
基金Supported by the Key Project Foundation of Fujian Province (No. 200I011)
文摘Silver has grown its attraction of the scientists in microelectronic field recently.Electrochemical deposition of silver onto copper substrates by immersion method has been one of the keen topics. In this study, ethanol was used as the plating solution in which some chemicals were added. The silver deposits were characterized by a field emission scanning electron microscopy （FESEM）, an atom force microscope （AFM）, a transmission electron microscope （TEM） and a selected area electron diffraction （SAED）. It was found that silver immersion using ethanol-based bath has good coverage feature. The highlands of the copper substrate are coated by silver particles whose sizes are around 12 nm, but those sizes at low-lying lands are a little smaller.
基金supported by the National Key R&D Program of China(Grant No. 2017YFB0305702)。
文摘Two kinds of silver based medium temperature brazing filler metals(45AgCuZnSn and 60AgCuSn) were selected to braze and seal brass flange pipe and copper pipe by high frequency heating brazing. In this paper, the quality of the braze was evaluated by immersion ultrasound, and the microstructure of the brazed joint was observed by SEM and EDS. The experimental results show that the high frequency heating brazing can quickly achieve the device sealing;through the ultrasonic flaw detection image calculation, the brazed bonding rate obtained by 60AgCuSn brazing is 87%, and by 45AgCuZnSn brazing is 71%;the cross-sectional area of the brazed joint obtained by two kinds of silver based medium temperature brazing filler metals is observed, the brazed joint obtained by 45AgCuZnSn brazing has defects visual, and a large amount of Zn element gathered in the defects, there is no obvious porosity in the brazed joint by 60AgCuSn brazing,and the bonding layer is dense and coherent. Through the contrast test, the choice of 60AgCuSn alloy brazing can meet the needs of high frequency brazing of brass flange pipe and copper pipe.