摘要
Al_(86)Ni_(8)Co_(1)La_(1)Y_(2)Gd_(2) amorphous coatings were prepared using cold gas kinetic spray technology.The results show that Al_(86)Ni_(8)Co_(1)La_(1)Y_(2)Gd_(2) amorphous coatings are achieved with the porosity about 3.2%,thickness about 893 μm,the amount of amorphous phase about 82.5%,the hardness about 300 HV0.2.The corrosion potential and anti-corrosion life of 7075 T6 alloy aluminum are about-0.78 V and 72 h,respectively.The electrochemical analysis and neutral salt spray are about-0.69 V corrosion potential and 274 h anti-corrosion life for amorphous Al-based coatings,respectively.Therefore,the life of the Albased amorphous coatings is about 3.8 times that of 7075 T6 aluminum alloy.Besides,the failure mechanism was analyzed using TEM in this investigation.In a word,Al_(86)Ni_(8)Co_(1)La_(1)Y_(2)Gd_(2) coatings keep dense structure,high amorphous content,favorable amorphous phase stabilizing ability and longer anticorrosion life.That is,Al_(86)Ni_(8)Co_(1)La_(1)Y_(2)Gd_(2) coatings have better comprehensive properties.Therefore,these findings indicate that the present Al_(86)Ni_(8)Co_(1)La_(1)Y_(2)Gd_(2) amorphous coatings prepared using cold gas kinetic spray technique can protect aluminum alloy very well and they can be considered to be used in aviation field.
基金
Project supported by the AVIC Unite Fund(KZ041605114)
Civil Aircraft(MJ-2016-F-16)。