摘要
Smelting separations of Hongge vanadium-bearing titanomagnetite metallized pellets（HVTMP）prepared by gas-based direct reduction were investigated,and the effects of smelting parameters on the slag/metal separation behaviors were analyzed.Relevant mechanisms were elucidated using X-ray diffraction analysis,FACTSAGE 7.0 calculations,and scanning electron microscopy observations.The results show that,when the smelting temperature,time,and C/O ratio are increased,the recoveries of V and Cr of HVTMP in pig iron are improved,the recovery of Fe initially increases and subsequently decreases,and the recovery of Ti O_2 in slag decreases.When the smelting Ca O/Si O_2 ratio is increased,the recoveries of Fe,V,and Cr in pig iron increase and the recovery of Ti O_2 in slag initially increases and subsequently decreases.The appropriate smelting separation parameters for HVTMP are as follows：smelting temperature of 1873 K;smelting time of 30–50 min;C/O ratio of 1.25;and Ca O/Si O_2 ratio of 0.50.With these optimized parameters（smelting time：30 min）,the recoveries of Fe,V,Cr,and Ti O_2 are 99.5%,91.24%,92.41%,and 94.86%,respectively.
Smelting separations of Hongge vanadium-bearing titanomagnetite metallized pellets（HVTMP）prepared by gas-based direct reduction were investigated,and the effects of smelting parameters on the slag/metal separation behaviors were analyzed.Relevant mechanisms were elucidated using X-ray diffraction analysis,FACTSAGE 7.0 calculations,and scanning electron microscopy observations.The results show that,when the smelting temperature,time,and C/O ratio are increased,the recoveries of V and Cr of HVTMP in pig iron are improved,the recovery of Fe initially increases and subsequently decreases,and the recovery of Ti O_2 in slag decreases.When the smelting Ca O/Si O_2 ratio is increased,the recoveries of Fe,V,and Cr in pig iron increase and the recovery of Ti O_2 in slag initially increases and subsequently decreases.The appropriate smelting separation parameters for HVTMP are as follows：smelting temperature of 1873 K;smelting time of 30–50 min;C/O ratio of 1.25;and Ca O/Si O_2 ratio of 0.50.With these optimized parameters（smelting time：30 min）,the recoveries of Fe,V,Cr,and Ti O_2 are 99.5%,91.24%,92.41%,and 94.86%,respectively.
基金
financially supported by the National Natural Science Foundation of China (No.51574067)