Phase transitions and magnetic properties of shape-memory materials can be tailored by tuning the size of the constituent materials, such as nanoparticles. However, owing to the lack of suitable synthetic methods for size-controlled Heusler nanoparticles, there is no report on the size dependence of their properties and functionalities. In this contribution, we present the first chemical synthesis of size-selected Co-Ni-Ga Heusler nanoparticles. We also report the structure and magnetic properties of the biphasic Co-Ni-Ga nanoparticles with sizes in the range of 30-84 nm, prepared by a SBA-15 nanoporous silica- templated approach. The particle sizes could be readily tuned by controlling the loading and concentration of the precursors. The fractions and crystallite sizes of each phase of the Co-Ni-Ga nanoparticles are closely related to their particle size. Enhanced magnetization and decreased coercivity are observed with increasing particle size. The Curie temperature （To） of the Co-Ni-Ga nanoparticles also depends on their size. The 84 nm-sized particles exhibit the highest Tc （≈ 1,174 K） among all known Heusler compounds. The very high Curie temperatures of the Co-Ni-Ga nanoparticles render them promising candidates for application in high-temperature shape memory alloy-based devices.
Phase transitions and magnetic properties of shape-memory materials can be tailored by tuning the size of the constituent materials, such as nanoparticles. However, owing to the lack of suitable synthetic methods for size-controlled Heusler nanoparticles, there is no report on the size dependence of their properties and functionalities. In this contribution, we present the first chemical synthesis of size-selected Co-Ni-Ga Heusler nanoparticles. We also report the structure and magnetic properties of the biphasic Co-Ni-Ga nanoparticles with sizes in the range of 30-84 nm, prepared by a SBA-15 nanoporous silica- templated approach. The particle sizes could be readily tuned by controlling the loading and concentration of the precursors. The fractions and crystallite sizes of each phase of the Co-Ni-Ga nanoparticles are closely related to their particle size. Enhanced magnetization and decreased coercivity are observed with increasing particle size. The Curie temperature （To） of the Co-Ni-Ga nanoparticles also depends on their size. The 84 nm-sized particles exhibit the highest Tc （≈ 1,174 K） among all known Heusler compounds. The very high Curie temperatures of the Co-Ni-Ga nanoparticles render them promising candidates for application in high-temperature shape memory alloy-based devices.