摘要
对W-Mo-Dy表面高速钢试样分别进行了1000、1050、1100℃淬火和550℃×1 h×3次回火,并在20、100、200、300、400、500℃和载荷5N下进行了高温摩擦性能试验。结果表明:在1000、1050、1100℃淬火后的试样在500℃磨损试验的平均摩擦系数分别为:0.15、0.1、0.09;在1050℃淬火的W-Mo-Dy表面稀土高速钢的高温耐磨性最佳,当磨损试验温度为400、500℃时,其磨损量分别是1000℃淬火试样的0.72、0.48倍,是1100℃淬火试样的0.35、0.47倍。
Quenching at 1000,1050 and 1100 ℃ and then tempering at 550 ℃ ×1 h ×3 times of W-Mo-Dy surface rare-earth high speed steel samples were carried out respectively, and high temperature friction performance test was done at20, 100, 200, 300, 400 and 500 ℃ under the load of 5N. The results show that average friction coefficient of samples quenched at1000, 1050, 1100 ℃ during wear test at 500℃ is 0.15, 0.1 and 0.09 respectively. High temperature wear resistance of W-Mo-Dy surface rare-earth high speed steel quenched at 1050 ℃ is the best. When the wear test temperature is 400 and 500 ℃,the amount of wear is 0.72 and 0.48 times of sample quenched at 1000 ℃, and 0.35, 0.47 times of sample quenched at 1100 ℃.
出处
《热加工工艺》
CSCD
北大核心
2017年第4期251-253,共3页
Hot Working Technology
基金
国家自然科学基金资助项目(51264007)
国家自然科学基金青年基金资助项目(51201043)
广西信息材料重点试验室重点项目(1210908-214-Z)
广西自然科学基金资助项目(2015GXNSFBA139214)
桂林电子科技大学研究生教育创新计划资助项目(YJCXB201501)
桂林电子科技大学-桂林电科院研究生联合培养基地专项经费资助项目(20141103-09-Z)
广西科学研究与技术开发科技攻关计划项目(桂科攻12118020-2-2-1)
关键词
表面高速钢
高温耐磨性
摩擦系数
surface high speed steel
high temperature wear resistance
friction coefficient