摘要
对某低品位含金硫精矿开展氧压酸浸产元素硫、碱硫氧压浸取金银试验。酸浸试验最佳条件为:浸出温度130℃、浸出时间300min、浸出压力1.6 MPa、液固比4:1、始酸浓度20g/L、木质素2‰;碱硫氧压浸金试验最佳条件为:浸金剂(石灰+硫磺)为总干矿的40%、硫碱质量比0.35、催化剂Cu(NH_3)_4^(2+)0.06mol/L、活化剂木质素占干矿的0.2%、氧压0.4 MPa、温度105℃、浸金时间5h,在此条件下金、银的浸出率分别为88.23%和61.35%。
Gold and silver were leached from low grade gold-bearing sulfur concentrates by alkali-sulfur oxygen pressure leaching. The optimum acidic leaching conditions including leaching temperature of 130 ℃, leaching time of 300 min, leaching pressure of 1.6 MPa, L/S of 4 ： 1, initial concentration of acid of 20 g/L, and lignin of 2‰. The optimum sulfur-alkali oxygen pressure leaching conditions include leaching agent of 40% of total dry ore, mass rate of sulfur to alkali of 0.35, catalyst Cu（NH3）42＋ of 0. 06 mol/L, sodium lignosulphonate of 0. 2% of dry ore, oxygen pressure of 0.4 MPa, temperature of 105℃ , and leaching time of 5 h. The leaching rate of gold and silver is 88.23 % and 61.35 % respectively under these optimum conditions.
出处
《有色金属（冶炼部分）》
CAS
北大核心
2016年第9期31-34,54,共5页
Nonferrous Metals（Extractive Metallurgy)
关键词
碱硫氧压浸出
低品位含金硫硫精矿
酸浸
alkali-sulfur oxygen pressure leaching
low grade gold-bearing sulfur concentrates
acid leaching