本文简述了不锈钢焊接接头的各种腐蚀机理作了分析讨论,并提出了不锈钢焊接接头的晶间腐蚀、应力腐蚀开裂、腐蚀疲劳、选择性腐蚀、点腐蚀、脆裂等的防护措施。
In this article,different mechanism of corrosion in welding joint of stainless steel are briefed. The mesasure to prevent intergranular corrosion,stress corrosion cracking,corrosion fatigue,selective corrosion,pitting and cracking etc. are suggested.