摘要
以NiSO4、ZnSO4和Nd(NO3)3为原料,采用共沉淀快速冷冻法制备出了复合掺杂稀土Nd(Ⅲ)和Zn(Ⅱ)的非晶态氢氧化镍粉体材料。测试发现:样品材料微结构无序性强,结晶水含量较高。将样品材料制备成镍电极并组装成MH-Ni电池,在80 mA/g恒电流充电5.5 h、40 mA/g恒电流放电、终止电压为1.0 V的充放电制度下,复合掺杂6%Nd(Ⅲ)和6%Zn(Ⅱ)样品材料电池的放电平台为1.262 4 V,放电比容量为343.12 mAh/g,远高于目前应用的β-Ni(OH)2电极活性材料的放电比容量。
Amorphous nickel hydroxide eodoped in rare earth Nd （III） and Zn （II） can be synthesized by the method of quick cryoprecipition with NiSO4, ZnSO4 and Nd （ NO3 ） 3. The characterization shows that the microstructure of sample contains some crystal water,and the disordering degree is strong. A simulated MH-Ni battery composed of amorphous nickel hydroxide particles as activity material is assembled. When the sample codoped in 6% Nd（III） and 6%Zn（II） is charged at 80 mA/g for 5.5 h and discharged at 40 mA/g to a cut-off potential of 1.0 V, the discharge voltage plateau is smooth at 1. 262 4 V, the discharge specific capacity can reach as 343.12 mAh/g, higher than discharge specific capacity of β-Ni（OH） 2 electrode activity material.
出处
《桂林工学院学报》
北大核心
2009年第4期502-506,共5页
Journal of Guilin University of Technology
基金
国家自然科学基金资助项目(20563001)
广西科学研究与技术开发计划项目(桂科能05112001-2A1)
广西区教育厅科研项目(桂教科研[2005]47)
广西研究生教育创新人才基地资助项目(桂学位[2007]18)
广西研究生教育创新计划资助项目(2008105960817M21)