The rare earth oxide Y2O3 was added to the system Li2O—Al2O3—SiO2 glass—ceramics and the effects of Y2O3 on the properties of melting, crystallizing, microstruoture as well as thermal expansion coefficient of the glass was studied by DTA, SEM and XRD. The results indicate that, adding YZO3 to Li2O—Al2O3—SiO2 systems glass could increase the viscosity of glass melt, in6rease the melting temperature and the crystallization temperature of glass,increase the volume fraction of crystals while the crystal types are not changed, and the coefficient of thermal expansion of glass-ceramics decreases with the increasing of Y2O3 content.
The rare earth oxide Y2O3 was added to the system Li2O—Al2O3—SiO2 glass—ceramics and the effects of Y2O3 on the properties of melting, crystallizing, microstruoture as well as thermal expansion coefficient of the glass was studied by DTA, SEM and XRD. The results indicate that, adding YZO3 to Li2O—Al2O3—SiO2 systems glass could increase the viscosity of glass melt, in6rease the melting temperature and the crystallization temperature of glass,increase the volume fraction of crystals while the crystal types are not changed, and the coefficient of thermal expansion of glass-ceramics decreases with the increasing of Y2O3 content.
出处
《玻璃与搪瓷》
CAS
北大核心
1997年第4期1-7,共7页
Glass & Enamel
关键词
微晶玻璃
氧化钇
锂铝硅系统
玻璃
Rare earth oxide Glass-ceramics Coefficient of thermal expansion