摘要
以CdCl2·2.5H2O和碲粉为主要原料,在水相中反应制备CdTe前驱体,将其于500℃煅烧1h得到CdTeO3纳米颗粒。通过XRD、SEM和TEM对其物相和形貌进行了分析;并将其制成了气敏元件,进行气敏性能测试。结果表明:成功合成了单斜晶相的、平均粒径为100nm的CdTeO3纳米颗粒。以该材料制备的气敏元件对体积分数为50×10-6的乙醇有较高的灵敏度(15.1)和选择性。
CdCl2·2.5H20 and tellurium powder were used as main raw materials to prepare CdTe precursor in aqueous phase. And then it was calcined at 500 ℃ for 1 h. Obtained CdTeO3 nanoparticles were characterized by XRD, SEM and TEM. Gas sensors were prepared with CdTeO3 as active component and their gas-sensing properties were investigated. The results show that monoclinic CdTeO3 nanoparticles was successfully prepared, and its average size is about 100 nm. The sensors have good sensitivity （15.1） and selectivity to 50x 10^-6 ethanol （volume fraction）.