摘要
采用慢应变速率拉伸试验(SSRT)方法研究了温度(30~65℃范围)和电极电位(-1500^-200 mV(SCE)范围)对X70管线钢在0.5 mol/L Na2CO3+1 mol/L NaHCO3的高pH模拟土壤溶液中应力腐蚀破裂(SCC)行为的影响。结果表明:在阳极极化区,温度对该钢的SCC敏感性影响不大,在阴极极化区,SCC敏感性随温度升高而下降;在所研究的电位区间,SCC敏感性随着电极电位的降低而增大;SCC机理分析表明,当电位E>EH(溶液中H+/H2的平衡电位)时,应该是阳极溶解占主导,而当E≤EH时,氢致破裂占主导。
The behaviors of high pH stress corrosion cracking(SCC)of pipeline steel X70 in 0.5mol/L Na2CO3+1 mol/L NaHCO3 solution were studied by means of slow strain rate tests(SSRT) at different temperatures in the range from 30 ℃ to 65 ℃ and different electrode potentials from-1500 to-200 mV(SCE).The temperature had no apparent effect on SCC susceptibility of the steel in anodic polarization range,but the SCC susceptibility increased with the rise of temperature in cathodic polarization range.The SCC susceptibilit...