In high-speed machining,hardened steel materials are subjected to high temperatures and high strain rates.Under these conditions,the composition and microstructure of the material may change,and phenomena,such as ther...In high-speed machining,hardened steel materials are subjected to high temperatures and high strain rates.Under these conditions,the composition and microstructure of the material may change,and phenomena,such as thermal softening,emerge.These effects are difficult to detect by only observing the chip morphology.Here,using a microscopic detection method,the dynamic mechanical behavior and microstructure of SDK11 hardened steel(62HRC)is investigated at high temperature and high strain-rate,and the relationship between strain hardening,thermal softening,and strain-rate strengthening is determined.The metallographic phases of specimens treated using a split-Hopkinson pressure bar,and″chips″generated during high-speed machining at high temperature and high strain rate state are compared.The results indicate that the phase composition at low temperature and low strain rate differs from that at high temperature and high strain rate.It is further concluded that shear slip occurs at high temperature and high strain rate,and the shear behavior is more pronounced at higher strain rates.展开更多
Sr0.6 Ba0.4 Nb2 O6 micro-rods are prepared by the molten-salt method with K2 SO4,KCl-K2 SO4,and KCl as fluxes.It reveals that the Sr0.6 Ba0.4 Nb2 O6 synthesized with KCl as a flux exhibits a single phase with tetragon...Sr0.6 Ba0.4 Nb2 O6 micro-rods are prepared by the molten-salt method with K2 SO4,KCl-K2 SO4,and KCl as fluxes.It reveals that the Sr0.6 Ba0.4 Nb2 O6 synthesized with KCl as a flux exhibits a single phase with tetragonal tungsten bronze structure.The measurement of X-ray diffraction indicates that the Sr0.6 Ba0.4 Nb2 O6 micro-rods synthesized at 1 300℃are anisotropic.The morphology of the powers is examined by transmission electron microscope.It reveals that the length-diameter ratio of Sr0.6 Ba0.4 Nb2 O6 micro-rods increases with increasing annealing temperature from 900℃to 1 300℃.At 1 300℃,the rod possesses a large length-diameter ratio of 8∶1.Moreover,the analysis of the piezoelectric properties of single micro-rods using apiezo-response force microscope indicates that the domains of the material are arranged along its radial direction.展开更多
基金the Key Program of the NSFC-Guangdong Joint Fund,China(No.U1201245)
文摘In high-speed machining,hardened steel materials are subjected to high temperatures and high strain rates.Under these conditions,the composition and microstructure of the material may change,and phenomena,such as thermal softening,emerge.These effects are difficult to detect by only observing the chip morphology.Here,using a microscopic detection method,the dynamic mechanical behavior and microstructure of SDK11 hardened steel(62HRC)is investigated at high temperature and high strain-rate,and the relationship between strain hardening,thermal softening,and strain-rate strengthening is determined.The metallographic phases of specimens treated using a split-Hopkinson pressure bar,and″chips″generated during high-speed machining at high temperature and high strain rate state are compared.The results indicate that the phase composition at low temperature and low strain rate differs from that at high temperature and high strain rate.It is further concluded that shear slip occurs at high temperature and high strain rate,and the shear behavior is more pronounced at higher strain rates.
基金supported by the National Natural Science Foundation of China(No.11475086)
文摘Sr0.6 Ba0.4 Nb2 O6 micro-rods are prepared by the molten-salt method with K2 SO4,KCl-K2 SO4,and KCl as fluxes.It reveals that the Sr0.6 Ba0.4 Nb2 O6 synthesized with KCl as a flux exhibits a single phase with tetragonal tungsten bronze structure.The measurement of X-ray diffraction indicates that the Sr0.6 Ba0.4 Nb2 O6 micro-rods synthesized at 1 300℃are anisotropic.The morphology of the powers is examined by transmission electron microscope.It reveals that the length-diameter ratio of Sr0.6 Ba0.4 Nb2 O6 micro-rods increases with increasing annealing temperature from 900℃to 1 300℃.At 1 300℃,the rod possesses a large length-diameter ratio of 8∶1.Moreover,the analysis of the piezoelectric properties of single micro-rods using apiezo-response force microscope indicates that the domains of the material are arranged along its radial direction.