In this study, the influence of annealing processes for cold-rolled sheets on the microstructure and mechanical performance of ultra-pure 430 ferritic stainless steel was investigated. Thermo-Calc calculation, organiz...In this study, the influence of annealing processes for cold-rolled sheets on the microstructure and mechanical performance of ultra-pure 430 ferritic stainless steel was investigated. Thermo-Calc calculation, organization observation, SEM detection,and tensile tests were used to discern the optimal annealing process. It is found that the microstructure is made up by the fine and uniform recrystallized ferritic grains after annealing. The optimum annealing process for ultra-pure 430 stainless steel is 950 ℃ for 90 s. After annealing, the stainless steel can obtain the optimum microstructure,recrystallization texture, and mechanical properties.展开更多
In the present paper, the relations between the microstructure and the properties of Ti-14Al-21Nb and Ti-14Al-20Nb-3.5V-2Mo alloys at different temperatures and different cooling rates of heat treatment were re-vealed...In the present paper, the relations between the microstructure and the properties of Ti-14Al-21Nb and Ti-14Al-20Nb-3.5V-2Mo alloys at different temperatures and different cooling rates of heat treatment were re-vealed by X-ray , optical microscope , HVTEM , auto-graphical-analyser and mechanical properties test at roomand high temperature. The experimental results show as follows: at 1040～1120℃ 14h WQ, the microstruc-ture of Ti-14Al-21Nb bar is primary phaseα_2+B2. With temperature increasing, the primary α_2 phase de-crease and the mechanical properties ultimate tensile strength (UTS), yield strength (YS) and elongation(EL) at room temperature increase. When it has reduced the α_2 phase by 50% (at 1080℃/4h WQ) , the me-chanical properties at room temperature are excellent , EL being 10. 5%. Following the α_2 phase reduces contin-uously , UTS, YS are going up, but EL is going down. After heated at two phases range and cooled down tothe room temperature with furnace, the microstructure of Ti-14Al-20Nb-3.5V-2Mo alloy is the equiaxed α_2+needle-like α_2+βphase. The mechanical properties at room temperature and 700℃ are fairly good.展开更多
文摘In this study, the influence of annealing processes for cold-rolled sheets on the microstructure and mechanical performance of ultra-pure 430 ferritic stainless steel was investigated. Thermo-Calc calculation, organization observation, SEM detection,and tensile tests were used to discern the optimal annealing process. It is found that the microstructure is made up by the fine and uniform recrystallized ferritic grains after annealing. The optimum annealing process for ultra-pure 430 stainless steel is 950 ℃ for 90 s. After annealing, the stainless steel can obtain the optimum microstructure,recrystallization texture, and mechanical properties.
文摘In the present paper, the relations between the microstructure and the properties of Ti-14Al-21Nb and Ti-14Al-20Nb-3.5V-2Mo alloys at different temperatures and different cooling rates of heat treatment were re-vealed by X-ray , optical microscope , HVTEM , auto-graphical-analyser and mechanical properties test at roomand high temperature. The experimental results show as follows: at 1040～1120℃ 14h WQ, the microstruc-ture of Ti-14Al-21Nb bar is primary phaseα_2+B2. With temperature increasing, the primary α_2 phase de-crease and the mechanical properties ultimate tensile strength (UTS), yield strength (YS) and elongation(EL) at room temperature increase. When it has reduced the α_2 phase by 50% (at 1080℃/4h WQ) , the me-chanical properties at room temperature are excellent , EL being 10. 5%. Following the α_2 phase reduces contin-uously , UTS, YS are going up, but EL is going down. After heated at two phases range and cooled down tothe room temperature with furnace, the microstructure of Ti-14Al-20Nb-3.5V-2Mo alloy is the equiaxed α_2+needle-like α_2+βphase. The mechanical properties at room temperature and 700℃ are fairly good.