(Zr_(53)Al_(11.6)Ni_(11.7)Cu_(23.7))_(1−x)(Fe_(77.1)C_(22.9))_(x)(x=0−2.2,at.%)bulk metallic glasses(BMGs)were prepared by copper mold suction casting method.Their glass forming ability and physical and chemical prope...(Zr_(53)Al_(11.6)Ni_(11.7)Cu_(23.7))_(1−x)(Fe_(77.1)C_(22.9))_(x)(x=0−2.2,at.%)bulk metallic glasses(BMGs)were prepared by copper mold suction casting method.Their glass forming ability and physical and chemical properties were systematically investigated.The glass forming ability is firstly improved with increasing x,and then decreased when x exceeds 0.44 at.%.Both glass transition temperature and crystallization temperature are increased,while the supercooled liquid region is narrowed,with Fe−C micro-alloying.The hardness,yielding and fracture strength,and plasticity firstly increase and then decrease when x reaches up to 1.32 at.%.The plasticity of the BMG(x=1.32 at.%)is six times that of the Fe-free and C-free BMG.In addition,by the Fe−C micro-alloying,the corrosion potential is slightly decreased,while the corrosion current density increases.The pitting corrosion becomes increasingly serious with the increase of Fe and C content.展开更多
基金This work was supported by the National Natural Science Foundation of China(No.51871234)the National Key Research and Development Program of China(No.2016YFB-0300500)the Open Fund of Key Laboratory of Materials Preparation and Protection for Harsh Environment(Nanjing University of Aeronautics and Astronautics),China,and Ministry of Industry and Information Technology,China(No.XCA19013-04).
文摘(Zr_(53)Al_(11.6)Ni_(11.7)Cu_(23.7))_(1−x)(Fe_(77.1)C_(22.9))_(x)(x=0−2.2,at.%)bulk metallic glasses(BMGs)were prepared by copper mold suction casting method.Their glass forming ability and physical and chemical properties were systematically investigated.The glass forming ability is firstly improved with increasing x,and then decreased when x exceeds 0.44 at.%.Both glass transition temperature and crystallization temperature are increased,while the supercooled liquid region is narrowed,with Fe−C micro-alloying.The hardness,yielding and fracture strength,and plasticity firstly increase and then decrease when x reaches up to 1.32 at.%.The plasticity of the BMG(x=1.32 at.%)is six times that of the Fe-free and C-free BMG.In addition,by the Fe−C micro-alloying,the corrosion potential is slightly decreased,while the corrosion current density increases.The pitting corrosion becomes increasingly serious with the increase of Fe and C content.