Yttria-stabilized zirconia（ YSZ） coatings were deposited by low pressure plasma spray（ LPPS） in 1.0× 10^4 Pa,1.5 × 10^4 Pa,and 2.5 × 10^4 Pa. Both in-flight particle diagnostic detected by DPV-2000 ...Yttria-stabilized zirconia（ YSZ） coatings were deposited by low pressure plasma spray（ LPPS） in 1.0× 10^4 Pa,1.5 × 10^4 Pa,and 2.5 × 10^4 Pa. Both in-flight particle diagnostic detected by DPV-2000 system and ANSYS-FLUENT software were used to study the connection between the parameters of flying particles and the coating formation,which might help to recognize the relationship between the operation parameters and the coatings quality. The results of simulation showed that particles in a lower spray pressure could achieve a higher velocity. The particle velocity was around 380 m/s at a distance of 35 cm from the nozzle at 1.0 × 10^4 Pa while only 300 m/s at 2.5 × 10^4 Pa in actual measurement.The results showed that the velocity of particles increased with decreasing the spray pressure,which might enhance the flattening rate of coatings and thereby decreased the porosity. The deposited YSZ coating with the lowest porosity can be gained under 1.0 × 10^4 Pa condition.展开更多
An oxidation resistant Al-Cu-Fe quasicrystalline coating was fabricated on substrate of Ti alloy by low pressure plasma spraying (LPPS) method. As-sprayed Al-Cu-Fe coating has a rapidly solidified lamellar microstruct...An oxidation resistant Al-Cu-Fe quasicrystalline coating was fabricated on substrate of Ti alloy by low pressure plasma spraying (LPPS) method. As-sprayed Al-Cu-Fe coating has a rapidly solidified lamellar microstructure consisting of quasicrystalline phase and crystalline phase. The formation of quasicrystalline coating is related to the annealing. The results from the ox!dat!on experiments showed that Al-Cu-Fe quasicrystalline coating improved the oxidation resistance of Ti-base alloys. During the oxidation period there is no evident spallation of the coating from the substrate. Oxide formed on the surface of Al-Cu-Fe quasicrystalline coating after oxidation consisted of Al2O3. Oxidation occurs Ieading to a change of concentration and phase transformation in the coating surface. Selective oxidation of AI transforms the quasicrystalline phase into the phase.展开更多
基金financially supported by the National Natural Science Foundation of China(No.51301112, No.51401129)Natural Science Foundation of Liaoning Province of China(No.201602553 )+1 种基金China Postdoctoral Science Foundation(2015M571327)The Science Research Program of Education Department in Liaoning Province(No.L2014048)
文摘Yttria-stabilized zirconia（ YSZ） coatings were deposited by low pressure plasma spray（ LPPS） in 1.0× 10^4 Pa,1.5 × 10^4 Pa,and 2.5 × 10^4 Pa. Both in-flight particle diagnostic detected by DPV-2000 system and ANSYS-FLUENT software were used to study the connection between the parameters of flying particles and the coating formation,which might help to recognize the relationship between the operation parameters and the coatings quality. The results of simulation showed that particles in a lower spray pressure could achieve a higher velocity. The particle velocity was around 380 m/s at a distance of 35 cm from the nozzle at 1.0 × 10^4 Pa while only 300 m/s at 2.5 × 10^4 Pa in actual measurement.The results showed that the velocity of particles increased with decreasing the spray pressure,which might enhance the flattening rate of coatings and thereby decreased the porosity. The deposited YSZ coating with the lowest porosity can be gained under 1.0 × 10^4 Pa condition.
文摘An oxidation resistant Al-Cu-Fe quasicrystalline coating was fabricated on substrate of Ti alloy by low pressure plasma spraying (LPPS) method. As-sprayed Al-Cu-Fe coating has a rapidly solidified lamellar microstructure consisting of quasicrystalline phase and crystalline phase. The formation of quasicrystalline coating is related to the annealing. The results from the ox!dat!on experiments showed that Al-Cu-Fe quasicrystalline coating improved the oxidation resistance of Ti-base alloys. During the oxidation period there is no evident spallation of the coating from the substrate. Oxide formed on the surface of Al-Cu-Fe quasicrystalline coating after oxidation consisted of Al2O3. Oxidation occurs Ieading to a change of concentration and phase transformation in the coating surface. Selective oxidation of AI transforms the quasicrystalline phase into the phase.