The slices of Cu-Al-Mg alloys with thickness of 0.1mm were prepared. Some samples were activated at the temperature of 590°C and 620°C respectively. The secondary electron emission (SEE) factor (σ) was dete...The slices of Cu-Al-Mg alloys with thickness of 0.1mm were prepared. Some samples were activated at the temperature of 590°C and 620°C respectively. The secondary electron emission (SEE) factor (σ) was determined. The composition of surface and the electron binding energy were studied by means of XPS and AES. It is shown that the oxide mainly consisting of Al2O3 and MgO can be formed spontaneously at room temperature. This oxide layer exhibits lower electron binding energy, high σ and satisfactory stability.展开更多
文摘The slices of Cu-Al-Mg alloys with thickness of 0.1mm were prepared. Some samples were activated at the temperature of 590°C and 620°C respectively. The secondary electron emission (SEE) factor (σ) was determined. The composition of surface and the electron binding energy were studied by means of XPS and AES. It is shown that the oxide mainly consisting of Al2O3 and MgO can be formed spontaneously at room temperature. This oxide layer exhibits lower electron binding energy, high σ and satisfactory stability.