The coercivity mechanism of Nd Fe B magnets prepared by combination of strip casting with hydrogen decrepitation techniques was investigated. The microstructure of (Nd 0.935 Dy 0.065 ) 14.5 Fe 79.4 B 6.1 magnet was observed. The average grain size is about 6～12 μm. The magnetizing field dependence of the hardmagnetic properties for the (Nd 0.935 Dy 0.065 ) 14.5 Fe 79.4 B 6.1 and the temperature dependence of the coercivity for the Nd 14.5 Fe 79.4 B 6.1 were investigated. Results show that the coercivity for magnets prepared by the combination of strip casting with hydrogen decrepitation techniques is controlled by the nucleation mechanism.
The coercivity mechanism of Nd Fe B magnets prepared by combination of strip casting with hydrogen decrepitation techniques was investigated. The microstructure of (Nd 0.935 Dy 0.065 ) 14.5 Fe 79.4 B 6.1 magnet was observed. The average grain size is about 6～12 μm. The magnetizing field dependence of the hardmagnetic properties for the (Nd 0.935 Dy 0.065 ) 14.5 Fe 79.4 B 6.1 and the temperature dependence of the coercivity for the Nd 14.5 Fe 79.4 B 6.1 were investigated. Results show that the coercivity for magnets prepared by the combination of strip casting with hydrogen decrepitation techniques is controlled by the nucleation mechanism.
基金
ProjectsupportedbytheNationalNaturalScienceFoundationofChina ( 5 0 2 710 3 6)