Anisotropic Nd-Fe-B magnets were fabricated by the single stage hot deformation (SSHD) method. The magnetic properties of the anisotropic Nd-Fe-B magnets are as follows: the maximum energy product is 234.7 kJ·m-3 , remanence 1.16 T and coercivity 684.3 kA·m-1. A study of the relationship between microstructure and magnetic properties for the anisotropic Nd-Fe-B magnets was carried out. The results show that the grains of Nd2Fe14B have grown up preferentially along the direction perpendicular to the pressing direction.
Anisotropic Nd-Fe-B magnets were fabricated by the single stage hot deformation (SSHD) method. The magnetic properties of the anisotropic Nd-Fe-B magnets are as follows: the maximum energy product is 234.7 kJ·m-3 , remanence 1.16 T and coercivity 684.3 kA·m-1. A study of the relationship between microstructure and magnetic properties for the anisotropic Nd-Fe-B magnets was carried out. The results show that the grains of Nd2Fe14B have grown up preferentially along the direction perpendicular to the pressing direction.
基金
Project supported by the National Natural Science Foundation of China (50471100)
Shanghai Municipal Developing Foundation of Science & Technology (0452nm055)
Shanghai Education Commissions (04AB10)