摘要
采用液相沉淀法制备三盐基硫酸铅纳米粉体。在50℃反应条件下,对粉体粒度影响较大的工艺条件进行研究。利用透射电子显微镜对粉体微观形态进行分析。实验结果表明,适当优化制备工艺条件,可以制备出40nm左右的三盐基硫酸铅纳米粉体。
Tri\|base lead sulfate nano\|powder was prepared by means of liquid phase precipitation method.The process conditions having more effect on the particle size of tri\|base lead sulfate nano\|powder were studied at reaction temperature of 50℃.The micro\|structural morphology nano\|powder were analyzed by using transmission electron microscope.The results showed that the tri\|base lead sulfate nano\|powder with 44nm in diameter could be prepared under the optimal process conditions.
出处
《塑料科技》
CAS
2003年第2期20-23,共4页
Plastics Science and Technology