The microstructure and misorientation of ultrathin hot strip were analyzed by CSP technology using electron back scattered diffraction (EBSD) method and Autoforge finite element program. The experimental results showed that the finishing hot rolling microstructures were the mixture of recrystallized and deformed austenite. After phase transformation, ferrite grains embody substructures and dislocations, leading to the high strength and relatively low elongation rate of the ultrathin hot strip. The FEM simulation of strain mode and distribution in deformation area has been fulfilled. The simulation results are in good agreement with the theoretical analysis and experimental results.
The microstructure and misorientation of ultrathin hot strip were analyzed by CSP technology using electron back scattered diffraction (EBSD) method and Autoforge finite element program. The experimental results showed that the finishing hot rolling microstructures were the mixture of recrystallized and deformed austenite. After phase transformation, ferrite grains embody substructures and dislocations, leading to the high strength and relatively low elongation rate of the ultrathin hot strip. The FEM simulation of strain mode and distribution in deformation area has been fulfilled. The simulation results are in good agreement with the theoretical analysis and experimental results.
基金
This research is supported by the State Foundation for Key Projects, Fundamental Research on New Generation of Steels (No.G1998061500)