摘要
以豆粕为原料,加入醋酸乙烯-丙烯酸酯共聚乳液和聚合MDI交联剂制成改性豆粕胶黏剂;利用改性豆粕胶黏剂压制三层实木复合地板,探讨不同工艺参数对实木复合地板浸渍剥离性能的影响。结果表明:压制三层实木复合地板的最佳工艺为热压时间15min、热压单位压力0.7MPa、固化剂用量15%,在此条件下,三层实木复合地板浸渍剥离性能较佳,满足《实木复合地板》(GB/T 18103—2022)要求。
Soybean meal was used as raw material,vinyl acetate-acrylate copolymer emulsion and polymerized MDI crosslinker were added to make modified soybean meal adhesive,and the modified soybean meal adhesive was used to press the three-layer solid wood composite floor,and the effects of different process parameters on the impregnation and peeling performance of solid wood composite floor were discussed.The results show that the best process for pressing three-layer solid wood composite floor is that the hot pressing time is 15 min,the unit pressure of hot pressing is 0.7 MPa,and the amount of curing agent is 15%.Under this condition,the impregnation and peeling performance of three-layer solid wood composite floor is better and meets the requirements of the Solid Wood Parquet(GB/T 18103—2022).
作者
何静怡
邵鑫
刘笑航
庞久寅
HE Jingyi;SHAO Xin;LIU Xiaohang;PANG Jiuyin(Wood Material Science and Engineering Key Laboratory of Jilin Province,Beihua University,Jilin 132013,China)
出处
《北华大学学报（自然科学版）》
CAS
2024年第5期677-680,共4页
Journal of Beihua University（Natural Science）
基金
吉林省发展和改革委员会产业技术研究与开发项目(2021C041-6)
吉林省科技厅重点研发项目(20240302102GX)。