摘要
工业试生产了ZT740连铸坯,利用冷酸侵蚀法、钻屑化学分析法、氧/氮分析仪、扫描电镜+能谱分析等手段分别研究了连铸坯的组织和成分偏析,并分析了[N]、[H]、[O]气体含量,以及夹杂物的性质。结果表明,铸坯低倍组织评级结果良好;[N]、[H]、[O]气体平均含量分别为65.45×10^(-4)%、1.0×10^(-4)%和21.48×10^(-4)%,均达到高品质钻探钢管中气体含量的设计指标;此外,在连铸坯中,除P、S元素出现一定程度的偏析外,其他元素均呈均匀分布;铸坯中非金属夹杂物形貌为点状和球形,10μm以下的夹杂物占比达到70%以上,大型夹杂物很少。连铸坯质量满足生产高品质钻探管的要求。
Microstructure,composition and segregation of ZT1740 continuous cast slab for high-grade drilling pipe were studied by cold acid method,chemical analysis,SEM and EDS analysis,gas analyzer.Results show that the macrostructure is good,gas contents including[N],[H]and[O]are low and satisfy the design requirement of the slab used for drill pipe.Element segregation,inclusion size and distribution all meet the demands of the high-grade drilling pipe.
作者
刘敏
刘伟
冯小明
赖朝彬
LIU Min;LIU Wei;FENG Xiaoming;LAI Chaobin(Xinyu Iron and Steel Co.,Ltd.,Xinyu 338001,China;Faculty of Materials Metallurgy and Chemistry,Jiangxi University of Science and Technology,Ganzhou 341000,China;Tianjin Iron and Steel Co.,Ltd.,Tianjin 300301,China)
出处
《铸造技术》
CAS
2021年第10期839-844,共6页
Foundry Technology
基金
国家自然科学基金资助项目(51974139)
科技部科技计划项目资助(SQ2009GJC5005722)。
关键词
钻探管
连铸坯质量
低倍组织评级
夹杂物
high-grade drilling pipe
continuous cast slab
low magnification grade
inclusionl macrostructure