摘要
对巴马格eFK型假捻变形机进行改造,采用75 dtex/72 f全消光涤纶预取向丝(POY)和83 dtex/36 f半消光全拉伸丝(FDY),生产涤纶146 dtex全消光仿棉拉伸变形丝(DTY),探讨了生产工艺。结果表明:在拉伸速度550~600 m/min、拉伸比1.110~1.115、D/Y比1.60、拉伸变形温度195~200℃、定形温度155~160℃、预网络压力0.30 MPa的条件下,生产的146 dtex全消光仿棉DTY断裂强度为3.49 cN/dtex,断裂伸长率为18.88%,沸水收缩率为3.98%,卷曲收缩率为15.58%,产品经后道加工,棉型感良好、手感蓬松、光泽柔和,具有较好的吸湿和抗起球特性,已获得客户的认可。
The Barmag eFK false twisting machine was transformed,146 dtex full dull cotton-like polyester DTY was produced by using 75 dtex/72 f full dull polyester POY and 83 dtex/36 f semi-dull FDY,and the production process was discussed.The result show that under the conditions of speed of 550~600 m/min,draw ratio of 1.110~1.115,D/Y of 1.60,texturing temperature of 195~200℃,setting temperature of 155~160℃,pe-interlaceing pressure of 0.30 MPa,the breaking strength of full dull cotton-like pelyester DTY is about 3.5 cN/dtex,the elongation at breat is 18.8%,the boiling water shrinkage is 3.98%and the crimp shrinkage is 15.58%.After processing the product has good cotton type feeling,fluffy touch,soft luster and good moisture absorption and anti-pilling properties.It has been recognized by customers.
作者
陈杰
陈志强
郑永伟
国世荣
崔利
陈伟群
CHEN Jie;CHEN Zhi-qiang;ZHENG Yong-wei;GUO Shi-rong;CUI Li;CHEN Wei-qun(Xinfengming Group Co.,Ltd.,Tongxiang 314513,Zhejiang,China;Zhejiang Technology Innovation Service Center,Hangzhou 310072,Zhejiang,China;Xinfengming Group Huzhou Zhongshi Technology Co.,Ltd.,Huzhou 313021,Zhejiang,China)
出处
《合成纤维》
CAS
2021年第6期14-16,共3页
Synthetic Fiber in China
基金
浙江省重点研发计划(2020C01142)。