摘要
利用共沉淀反应,以十二烷基苯磺酸钠(SDBS)为表面活性剂,合成了扇形分级微纳米碳酸钙。通过扫描电子显微镜(SEM)和X射线衍射仪(XRD)对样品进行分析和表征,结果表明扇形分级微纳米碳酸钙的长度为1~3μm,由粒径约为100 nm的粒子聚集而成。实验考察了碳酸钠溶液pH和反应温度对产物的影响,研究发现碳酸钠溶液pH对碳酸钙形状的调控起着极其重要的作用,低温下更有利于亚稳晶型球霰石的生成。
Hierarchical fan-shaped calcium carbonate with micro/nanostructures(HFCC)were synthesized by facile co-precipitation method in the presence of sodium dodecylbenzene sulfonate(SDBS).The samples were characterized by SEM and XRD.TheresultsshowedthatHFCCwithlengthof1?3滋mwerecomposedofnanoparticleswithsizeofabout100nm.Theeffects of temperature and pH of sodium carbonate solution on products were analyzed.Results showed that pH of sodium car-bonate solution played an important role in controlling the morphologies of calcium carbonate.Metastable vaterite crystals can be favorably obtained at low temperature.
作者
陈银霞
纪献兵
晋利
景长勇
Chen Yinxia;Ji Xianbing;Jin Li;Jing Changyong(Hebei University ofEnvironmental Engineering,Qinhuangdao 066102,China)
出处
《无机盐工业》
CAS
北大核心
2018年第4期30-32,共3页
Inorganic Chemicals Industry
基金
河北省自然科学基金资助项目(E2016415002
E2016415004)
河北省科技计划项目(15213620
15213629)
河北省高等学校科学技术研究项目(QN2016032)
秦皇岛市科技支撑计划项目(201401A023
201401A039)
河北环境工程学院博士启动基金项目(B201407
B201408)
关键词
碳酸钙
微纳米
分级结构
合成
calcium carbonate
micro/nanostructures
hierarchical structure
synthesis