Nanopowder MnO 2 was prepared with two oxidation reduction methods.XRD,SEM,FT IR and surface area measurement techniques were used to investigate properties of the MnO 2 powder.The results showed that the nano MnO 2 with an average diameter in 30～50nm and good dispersity and high catalytic activity for H 2O 2 decomposition,can be synthesized with the two methods.With reduced crystal size of the powder,the infrared absorption peak of Mn O bond was blue shifted and fissioned,one shifted 61 19cm -1 and the other shifted 11 15cm -1 ,and the characteristic vibration bands of adsorption water were also blue shifted.
Nanopowder MnO 2 was prepared with two oxidation reduction methods.XRD,SEM,FT IR and surface area measurement techniques were used to investigate properties of the MnO 2 powder.The results showed that the nano MnO 2 with an average diameter in 30～50nm and good dispersity and high catalytic activity for H 2O 2 decomposition,can be synthesized with the two methods.With reduced crystal size of the powder,the infrared absorption peak of Mn O bond was blue shifted and fissioned,one shifted 61 19cm -1 and the other shifted 11 15cm -1 ,and the characteristic vibration bands of adsorption water were also blue shifted.
出处
《化学研究与应用》
CAS
CSCD
北大核心
2002年第5期583-586,共4页
Chemical Research and Application
基金
陕西省自然科学基金 ( 2 99H16 )
教育厅科研专项基金 ( 0 0JK133)
陕西省物理无机重点实验室基金资助课题