Transition and fracture shift behavior in LCF test of dissimilar welded joint at elevated temperature 被引量:2

Transition and fracture shift behavior in LCF test of dissimilar welded joint at elevated temperature
原文传递
导出
摘要 This work focused on the low-cycle fatigue (LCF) behavior of modified 9Cr/CrMoV dissimilar welded joint at elevated temperature. Narrow gap submerged arc welding (NG-SAW) process via multi-pass and multi-layer techniques was employed to fabricate the welded joint. LCF tests at different strain amplitude range from 0.22% to 0.75% were performed at strain ratio R = -1. The two-slope behavior based on fracture location shift was presented both on the cyclic stress-strain (CSS) curve and Manson-Coffin (M-C) curve, which could be applied to predict the fatigue life more precisely especially at relatively low strain amplitude. The results indicated that the joint failed in CrMoV-base metal (BM) at relatively low strain amplitude below 0.4% while failure shifted to CrMoV-over tempered zone (OTZ) at higher strain amplitude above 0.4%. Fatigue failure occurred in CrMoV-BM at low strain amplitude could be attributed to temperature softening effect in CrMoV-BM combined with cyclic strengthening in CrMoV- OTZ. While CrMoV-OTZ with a comparable number of grain boundaries and much lower hardness than that of CrMoV-BM was deemed to be the weakest zone across the welded joint at higher strain amplitude. EBSD investigations also revealed that CrMoV-BM experienced more fatigue damage at relatively low strain amplitude, while CrMoV-OTZ accumulated more plastic strain at higher strain amplitude. This work focused on the low-cycle fatigue (LCF) behavior of modified 9Cr/CrMoV dissimilar welded joint at elevated temperature. Narrow gap submerged arc welding (NG-SAW) process via multi-pass and multi-layer techniques was employed to fabricate the welded joint. LCF tests at different strain amplitude range from 0.22% to 0.75% were performed at strain ratio R = -1. The two-slope behavior based on fracture location shift was presented both on the cyclic stress-strain (CSS) curve and Manson-Coffin (M-C) curve, which could be applied to predict the fatigue life more precisely especially at relatively low strain amplitude. The results indicated that the joint failed in CrMoV-base metal (BM) at relatively low strain amplitude below 0.4% while failure shifted to CrMoV-over tempered zone (OTZ) at higher strain amplitude above 0.4%. Fatigue failure occurred in CrMoV-BM at low strain amplitude could be attributed to temperature softening effect in CrMoV-BM combined with cyclic strengthening in CrMoV- OTZ. While CrMoV-OTZ with a comparable number of grain boundaries and much lower hardness than that of CrMoV-BM was deemed to be the weakest zone across the welded joint at higher strain amplitude. EBSD investigations also revealed that CrMoV-BM experienced more fatigue damage at relatively low strain amplitude, while CrMoV-OTZ accumulated more plastic strain at higher strain amplitude.
出处 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 2018年第4期720-731,共12页 材料科学技术(英文版)
关键词 Low-cycle fatigue 9Cr/CrMoV dissimilar welded joint Elevated temperature Fracture transition EBSD analysis Low-cycle fatigue 9Cr/CrMoV dissimilar welded joint Elevated temperature Fracture transition EBSD analysis
  • 相关文献

同被引文献3

引证文献2

二级引证文献9

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部