摘要
Three novel multi-microalloying TiAl-based alloys containing high Nb were designed and fabricated Thermogravimetric method was applied to investigate the influence of Cr on the oxidation behavior of high Nb TiAl alloy at 1,073 K for 200 h in laboratory air. The 2 at.% and 4 at.% Cr were added into the alloy,(respectivel named 2 Cr and 4 Cr compared to the Cr-free ternary alloy, 0 Cr alloy). The alloys' microstructure and compositio as well as the composition distribution of the oxidation scale were analyzed by means of Scanning Electro Microscopy(SEM), Energy Dispersive Spectroscopy(EDS), and X-Ray Diffractometry(XRD). The results show that the addition of Cr decreases the grain size of the Nb-TiAl alloy and leads to a transformation from a full lamellar structure to a nearly fully lamellar structure. When oxidized at 1,073 K for 200 h, the oxidized mass gai of the alloy increases with an increase in Cr addition amount in the first 100 h and decreases in the last 100 h With the increase of Cr content, the oxidation surface turns compact but uneven in morphology, which may affec the oxidation resistance of the alloy by increasing the peeling off risk of the oxidation layer at friction conditions.
Three novel multi-microalloying TiAl-based alloys containing high Nb were designed and fabricated Thermogravimetric method was applied to investigate the influence of Cr on the oxidation behavior of high Nb TiAl alloy at 1,073 K for 200 h in laboratory air. The 2 at.% and 4 at.% Cr were added into the alloy,（respectivel named 2 Cr and 4 Cr compared to the Cr-free ternary alloy, 0 Cr alloy）. The alloys＇ microstructure and compositio as well as the composition distribution of the oxidation scale were analyzed by means of Scanning Electro Microscopy（SEM）, Energy Dispersive Spectroscopy（EDS）, and X-Ray Diffractometry（XRD）. The results show that the addition of Cr decreases the grain size of the Nb-TiAl alloy and leads to a transformation from a full lamellar structure to a nearly fully lamellar structure. When oxidized at 1,073 K for 200 h, the oxidized mass gai of the alloy increases with an increase in Cr addition amount in the first 100 h and decreases in the last 100 h With the increase of Cr content, the oxidation surface turns compact but uneven in morphology, which may affec the oxidation resistance of the alloy by increasing the peeling off risk of the oxidation layer at friction conditions.
基金
financially supported by the Fundamental Research Funds for the Central Universities of Ministry of Education of China(Grant Nos.HEUCFP 201731 and 201719)