摘要
利用金相显微镜、扫描电子显微镜和X射线衍射分析等方法研究了服役50 000 h后P92钢焊缝金属的组织变化。结果表明,服役前P92钢焊缝金属析出相主要为细小颗粒状的M23C6,服役50 000 h后马氏体板条依然清晰,组织中析出相数量显著增多,除M23C6相外沿晶界和板条界分布了大量的块状Laves相,其数量和尺寸均大于M23C6相。这将对P92钢焊缝金属的性能产生不利影响。
Microstructure evolution of P92 steel weld metal after serving for 50 000 h was investigated by means of optical microscopy, electron microscopy, X-ray diifractometer and so on. The results show that the precipitates in the P92 steel weld metal are mainly fine granular 23C6 before service. After serving for 50 000 h, martensito lath in the weld metal remains clear. However, the amount of precipitates increases apparently. In addition to M23C6, a lot of block Laves phases are distributed along the grain boundary and lath boundary. The amount and size of Laves phases are bigger than those of 23C6 phase, which results in detrimental influence on the properties of the weld metal.
出处
《热加工工艺》
CSCD
北大核心
2017年第19期208-210,共3页
Hot Working Technology
关键词
超超临界机组
P92钢
焊缝金属
组织
析出相
ultra supercritical unit
P92 steel
weld metal
microstructure
precipitation