摘要
In order to found new dielectrics ceramics in tungsten bronze structure, unfilled tungsten bronze（TB） ceramics with nominal formula Ba4PrFe（0.5）Nb（9.5）O（30） were prepared by the solid state reaction method. The microstructure and dielectric properties were studied using powder X-ray diffraction, field emission scanning electron microscope, and variable temperature dielectric test system. The results show that the ceramics have a single phase and belong to the space group of P4bm with the cell of a = b = 12.4839（3） ？, c = 3.9409（5） ？, V = 614.192（2） ？3. The frequency dependent dielectrics properties show that the ceramics have a Debye-like relaxation at room temperature, while the temperature dependent dielectrics properties indicate that the ceramics are a relaxor and the relaxation is due to the nanopolars and oxygen vacancies. The ceramics have a potential application in electronic ceramics as temperature-stable multilayer ceramic capacitors.
In order to found new dielectrics ceramics in tungsten bronze structure, unfilled tungsten bronze（TB） ceramics with nominal formula Ba4PrFe（0.5）Nb（9.5）O（30） were prepared by the solid state reaction method. The microstructure and dielectric properties were studied using powder X-ray diffraction, field emission scanning electron microscope, and variable temperature dielectric test system. The results show that the ceramics have a single phase and belong to the space group of P4bm with the cell of a = b = 12.4839（3） ？, c = 3.9409（5） ？, V = 614.192（2） ？3. The frequency dependent dielectrics properties show that the ceramics have a Debye-like relaxation at room temperature, while the temperature dependent dielectrics properties indicate that the ceramics are a relaxor and the relaxation is due to the nanopolars and oxygen vacancies. The ceramics have a potential application in electronic ceramics as temperature-stable multilayer ceramic capacitors.
基金
Funded by the National Natural Science Foundation of China(11564009)
the Natural Science Foundation of Guangxi Province(2013GXNSFBA019230 and 2014GXNSFAA118350)
the Open Founding of Guangxi Ministry-Province Jointly-Constructed Cultivation Base for State Key Laboratory of Processing for Nonferrous Metal and Featured Materials(13KF-17 and 15KF-12)