热处理对X90管线钢组织性能的影响 被引量:6

Effect of heat treatment on microstructure and mechanical properties of X 90 pipeline steel
下载PDF
导出
摘要 将焊接的与未焊接的X90管线钢固溶后保温不同时间,对其显微组织和拉伸性能进行了分析.结果表明,X90管线钢在不同保温时间下的组织均由多边形铁素体和粒状贝氏体组成.随着保温时间的延长,粒状贝氏体由弥散状变为团状,M-A岛的含量增多,铁素体平均晶粒尺寸增大.焊接的与未焊接的实验钢保温时间为30 min,抗拉强度分别达最高660 MPa和725 MPa;保温60 min时抗拉强度分别最低为603 MPa和647 MPa.析出强化和细晶强化对钢的力学性能都有贡献,在保温30 min时,析出强化占主导地位.热处理对X90管线钢的性能影响对于经过焊接的与未焊接的实验钢,表现出了同样的趋势. Welded and not welded X90 pipeline steels were heated at a certain temperature and then kept the temperature for different time.Microstructure and mechanical properties were analyzed.The results showed that all X 90 pipeline steel specimens consist of polygonal ferrite and granular bainite.Granular bainite becomes agglomerates from a dispersed state,volume fraction of M- A islands increases,and average grain size of the ferrite increases with the increasing temperature preserving time.Tensile strengths reach highest values(660 MPa and 725 MPa,respectively)when the preserving time is 30 min for welded and not welded steels.The strengths become the lowest(603 MPa and647 MPa,respectively) when the preserving time is 60 min.The contribution comes from the precipitation and grain refinement strengthenings.When the preserving time is 30 min,the main contribution is the precipitation strengthening.There is a same trend through heat treatment of X90 pipeline steels for welded and not welded specimens.
出处 《材料与冶金学报》 CAS 北大核心 2016年第3期225-229,236,共6页 Journal of Materials and Metallurgy
基金 国家863科研项目(2015AA03A501) 东北大学国家重点实验室开放课题(12SYS05) 辽宁省教育厅系列项目(018-1502153601) 沈阳航空航天大学大学生创新创业训练计划项目(X1611105)
关键词 X90管线钢 粒状贝氏体 晶粒尺寸 力学性能 焊接 X90 pipeline steel granular bainite grain size mechanical properties weld
  • 相关文献

参考文献2

二级参考文献14

  • 1冯耀荣,高惠临,霍春勇,等.管线钢显微组织分析与鉴别[M].西安:陕两科学技术出版社,1995. 被引量:1
  • 2ARAKI T.Atlas for Bainitie Mierostruetures[J].ISIJ Inter.,1992(1):4-5. 被引量:1
  • 3CIZEK P,WYNNE B P,DAVIES C H J,et al.Effect of Composition and Austenite Deformation on the Transformation Characteristics of Low-Carbon and Uhralow-Carbon Microalloyed Steels[J].Metal.Trans.A,2002,33A (5):1331-1349. 被引量:1
  • 4BRAMFITT B L,SPEER J G.A Perspective on the Morphology of Bainite[J].Metal.Trans.A,1990,21A (3):817-829. 被引量:1
  • 5KRAUSS G,THOMPSON S W.Ferrite Mierostructure in Continuously Cooled Low and Uhralow Carbon Steels[J].ISIJ Inter.,1995,35 (8):937-945. 被引量:1
  • 6THOMPSON S W,COLVIN D J,KRAUSS G.Continuous Cooling Transformations and Micostruetures in a Low-Carbon,High-Strength Low-Alloy Plate Steel[J].Metal.Trans.A,1990,21 A(6):1493-1507. 被引量:1
  • 7ARAKI T.Mierostructure Aspects of Bainite and Bainire-Like Ferrite Structure of Continuously Cooled Low Carbon Steels[J].Materials Trans.JIM,1991,32 (8):729-736. 被引量:1
  • 8WILSON E A.The γ→а Transformation in Low Carbon Irons[J].ISIJ Inter.,1994,34 (8):615-630. 被引量:1
  • 9OHMORI Y.Bainite Transformations in Extremly Low Carbon Steels[J].ISIJ Inter.,1995,35 (8):962-968.x. 被引量:1
  • 10BHADESHIA H K D H,CHRISTIAN J W.Bainite in Steels[J].Metal.Trans.A,1990,21A (3):767-797. 被引量:1

共引文献11

同被引文献39

引证文献6

二级引证文献15

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部