研究主体材料并用比以及石蜡油、碳酸钙和乙烯丙烯酸树脂用量对氢化苯乙烯-丁二烯-苯乙烯嵌段共聚物(SEBS)/聚丙烯(PP)热塑性弹性体(TPE)性能的影响。结果表明:随着SEBS/PP并用比减小,TPE的邵尔A型硬度和压缩永久变形增大;当石蜡油用量为70份时,TPE的拉伸强度最大,压缩永久变形最小;碳酸钙用量增大,TPE的压缩永久变形减小;添加乙烯丙烯酸树脂,TPE的压缩永久变形先减小后增大,最佳用量为3份。
The effects of the blending ratio of main materials,and the addition level of paraffin oil,calcium carbonate,vinyl acrylic resin on the properties of hydrogenated styrene-butadiene-styrene block copolymer（SEBS）/polypropylene（PP） thermoplastic elastomer（TPE） were investigated. The results showed that,as SEBS/PP blending ratio decreased,the Shore A hardness and compression set of TPE increased. When the addition level of paraffin oil was 70 phr,the tensile strength of TPE was at the maximum and the compression set was at the minimum. As the addition level of calcium carbonate increased,the compression set of TPE decreased. Vinyl acrylic resin could reduce the compression set of TPE,and minimum compression set was obtained at 3 phr vinyl acrylic resin.
出处
《橡胶工业》
CAS
2016年第6期329-331,共3页
China Rubber Industry