The hot deformation behavior of Ti22A125 Nb was investigated by hot compression test.The flow stressstrain curves can be divided into two types：conventional dynamic recrystallization（DRX） and discontinuous DRX.The different softening mechanism and micro structure observation of conventional DRX and discontinuous DRX were analyzed.The processing map（PM） of Ti22A125 Nb was built to predict the safe deformation region.The optimal low strain rate domain（DOM I） with high power dissipation efficiency indicates the complete DRX.Additionally,in the high strain rate and low-temperature domain（DOM Ⅲ）,the power dissipation efficiency is low and some adiabatic shear bands and glide bands are observed,which are unsafe and should be avoided.Finally,the DRX map was established.In DOM I,it reveals low dislocation density and high DRX content,which is in agreement with PM.
The hot deformation behavior of Ti22A125 Nb was investigated by hot compression test.The flow stressstrain curves can be divided into two types：conventional dynamic recrystallization（DRX） and discontinuous DRX.The different softening mechanism and micro structure observation of conventional DRX and discontinuous DRX were analyzed.The processing map（PM） of Ti22A125 Nb was built to predict the safe deformation region.The optimal low strain rate domain（DOM I） with high power dissipation efficiency indicates the complete DRX.Additionally,in the high strain rate and low-temperature domain（DOM Ⅲ）,the power dissipation efficiency is low and some adiabatic shear bands and glide bands are observed,which are unsafe and should be avoided.Finally,the DRX map was established.In DOM I,it reveals low dislocation density and high DRX content,which is in agreement with PM.
基金
financially supported by the National Natural Science Foundation of China(No.51175431)