3~5μm波段耐高温低发射率涂层抗热震性能研究 被引量:6

Thermal Shock Resistance of Low Emissivity Coatings in 3—5 μm Band with High Temperature Resistance
下载PDF
导出
摘要 为了提高3~5μm波段耐高温低发射率涂层的抗热震性能,研究了添加剂MgO含量对涂层抗热震性能的影响。采用DIL 402C热膨胀仪测定涂层的热膨胀系数,用IR-2型发射率测试仪测定涂层在3~5μm波段的发射率,并用扫描电镜(Scanning electron microscope,SEM)对样品进行了表征。结果表明,当加入3%的MgO时,涂层与基板的热膨胀系数差最小,抗热震性能最优,达到50次;并且加入添加剂后的涂层仍然满足低发射率的要求,发射率最低为0.212。 To improve the thermal shock resistance of low emissivity coatings in 3—5μm wave band with high temperature resistance,the effect of the content of MgO on the thermal shock performance of coatings is investigated.The thermal expansion coefficient of coatings is tested by DIL 402 C.The emissivity in 3—5μm band of the coating is measured by IR-2and the surface morphology of the coatings is characterized by the scanning electron microscope(SEM).The results of experimental investigation indicate that when the content of MgO is 3%,the thermal expansion coefficient difference between the coating and the substrate is the minimum and the thermal shock resistance is the best,which reaches 50 times.The requirement of low emissivity is still met after adding additives,and the lowest emissivity is 0.212.
出处 《南京航空航天大学学报》 EI CAS CSCD 北大核心 2016年第1期48-52,共5页 Journal of Nanjing University of Aeronautics & Astronautics
基金 国家自然科学基金(90505008)资助项目 国家自然科学基金青年基金(51403102)资助项目 江苏省自然科学基金青年基金(SBK2014042556)资助项目 江苏高校优势学科建设工程资助项目
关键词 涂层 MGO 抗热震性能 热膨胀系数 低发射率 coatings MgO thermal shock resistance thermal expansion coefficient low emissivity
  • 相关文献

参考文献9

二级参考文献31

共引文献67

同被引文献34

引证文献6

二级引证文献19

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部