摘要
为了提高硅藻土与橡胶基体的相容性,采用干法改性工艺对硅藻土颗粒进行表面包覆改性并研究影响包覆改性效果的因素。结果表明,添加硬脂酸钙质量分数为5%的包覆改性剂,在转速为28 000 r/min时粉磨1 min,改性硅藻土样品的活化度达到90%,浊度达到853 NTU,可满足橡胶用填料的要求。
To improve the compatibility of diatomite and rubber matrix,the diatomite powders were modified by the dry method, and the influence of factors on modification effect was researched. The results show that by adding calcium stearate with mass fraction of 5% in modifier and grinding the diatomite at a speed of 28 000 r/min for 1 min, activation degree of the modified diatomite powders reaches 90%, and turbidity reaches 853 NTU.The sample can reach the requirements of rubber fillings.
出处
《中国粉体技术》
CAS
北大核心
2015年第5期76-78,共3页
China Powder Science and Technology
基金
中国建材非金属矿产地质总结研究项目
编号:12120114039901
关键词
硅藻土
表面改性
硬脂酸钙
diatomite
surface modification
calcium stearate