The effects of pyrolysis mode and pyrolysis parameters on Cl content in alumina were investigated, and the alumina products were characterized by XRD, SEM and ASAP. The experimental results indicate that the spray pyrolysis efficiency is higher than that of static pyrolysis process, and the reaction and evaporation process lead to a multi-plot state of the alumina products by spray pyrolysis. Aluminum phase starts to transform into γ-Al2O3 at spray pyrolysis temperature of 600 °C, which is about 200 °C lower than that of static pyrolysis process. The primary particle size of γ-Al2O3 product is 27.62 nm, and Cl content in alumina products is 0.38% at 800 °C for 20 min.
The effects of pyrolysis mode and pyrolysis parameters on Cl content in alumina were investigated, and the alumina products were characterized by XRD, SEM and ASAP. The experimental results indicate that the spray pyrolysis efficiency is higher than that of static pyrolysis process, and the reaction and evaporation process lead to a multi-plot state of the alumina products by spray pyrolysis. Aluminum phase starts to transform into γ-Al2O3 at spray pyrolysis temperature of 600 °C, which is about 200 °C lower than that of static pyrolysis process. The primary particle size of γ-Al2O3 product is 27.62 nm, and Cl content in alumina products is 0.38% at 800 °C for 20 min.
基金
Projects(U1202274,51004033,51204040)supported by the National Natural Science Foundation of China
Project(2012AA062303)supported by the National High Technology Research and Development Program of China
Project(2012BAE01B02)supported by the National Science and Technology Support Program of China
Project(L2014096)supported by the Education Department of Liaoning Province,China
Project(N130702001)supported by the Fundamental Research Funds for the Central Universities,China