采用回转窑对我国高硫铝土矿进行焙烧预处理,考察了焙烧温度、焙烧时间对矿物中硫含量及氧化铝溶出性能的影响,利用SEM和XRD技术对焙烧矿的微观形貌、晶型结构变化进行了分析,并对高硫矿脱硫机理和焙烧机理作了探讨.结果表明,焙烧脱硫处理高硫型铝土矿是可行的,焙烧温度为750℃、焙烧时间为60min时,焙烧矿中硫含量低于0.7%,达到我国氧化铝生产的工业要求;焙烧矿在溶出温度220℃、溶出时间60min的条件下,氧化铝溶出率达到97%以上.
Roasting pretreatment of high sulfur bauxite was studied using a rotary kiln, and the effects of roasting temperature and roasting time on sulfur content and digestion performance of high sulfur bauxite were examined. Changes of microscopic appearance and crystal structure were analyzed with SEM and XRD techniques. The mechanism of desulphurization and roasting pretreatment was also studied. The experimental results indicate that the sulfur in bauxite was successfully discharged as gas form through roasting, the sulfur content of high sulfur bauxite met the industrial standard under the conditions of 750℃ roasting temperature and 60 min holding time. The digestion rate of alumina was above 97% under the conditions of 220℃digestion temperature and 60 min holding time.
出处
《过程工程学报》
EI
CAS
CSCD
北大核心
2008年第5期892-896,共5页
The Chinese Journal of Process Engineering
基金
国家自然科学基金资助项目(编号:50644016
50704011)
国家重点基础研究发展规划(973)基金资助项目(编号:2007CB13504)
教育部高校博士点基金资助项目(编号:20050145029)
辽宁省优秀青年科技人才基金资助项目(编号:2005221012)
关键词
高硫铝土矿
回转窑焙烧
脱硫
溶出性能
high-sulfur bauxite
roasting
desulphurization
digestion performance