以废旧镁铬砖为主要原料，采用Al2O3微粉为结合剂、Ca（H2PO4）2为促烧剂制备了RH浸渍管喷补料，研究了Al2O3微粉和Ca（H2PO4）2加入量对材料性能的影响。工业应用试验表明：加入4％的Al2O3微粉及2.5％～3％的Ca（H2PO4）2时，材料性能最好；新型RH喷补料使用效果良好，实现了废旧镁铬砖的回收再利用，保护了环境。
RH snorkel gunning refractories were prepared using waste magnesia-chrome bricks as main starting materials, Al2O3 micropowder as binder, a right amount Ca （H2PO4）2 as acceleration sintering. Effects of Al2O3 micropowder and Ca（H2PO4）2 addition on properties of gunning refractories were studied. Industrial application results show that adding 4% Al2O3 micropowder and 2.5%~3% Ca（H2PO4）2 is the optimal addition. The new gunning refractories were good to use. The reuse of waste magnesia-chrome bricks is realized and environment is protected.