The hydro-abrasive erosion wear behavior of duplex-treated surfaces of AISI H13 tool steel

The hydro-abrasive erosion wear behavior of duplex-treated surfaces of AISI H13 tool steel
原文传递
导出
摘要 The influence of duplex surface treatments consisting of a DC-pulsed plasma nitriding process and subsequent coatings of CrN and TiAlN deposited by physical vapor deposition(PVD)on AISI H13 tool steel was studied in this article.The treated samples were characterized using metallographic techniques,SEM,EDS,and microhardness methods.Hydro-abrasive erosion wear tests were performed in a specifically designed wear tester in which the samples were rotated in a wear tank containing a mixture of distilled water and ceramic abrasive chips with a fixed rotational speed.The wear rates caused by the abrasive particle impacts were assessed based on accumulated weight loss measurements.The worn surfaces were also characterized using optical microscopy,SEM,and EDS.Microhardness measurements indicated a significant increase in the surface hardness of the duplex-treated samples.The surfaces of the samples with the TiAlN coating were approximately 15 times harder than that of the untreated samples and 3 times that of the plasma nitrided samples.Hydro-abrasive erosion wear results showed that the duplex surface treatments,especially the CrN coating,displayed the highest erosion wear resistance.
出处 《Science China(Technological Sciences)》 SCIE EI CAS 2014年第5期1040-1051,共12页 中国科学(技术科学英文版)
关键词 plasma nitriding physical vapor deposition duplex surface treatment MICROHARDNESS hydro-abrasive erosion wear 磨料颗粒 表面处理 冲蚀磨损 AISI 磨损行为 工具钢 H13 水力
  • 相关文献

参考文献2

二级参考文献16

共引文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部