Influence of double emulsions solidification rate on sphericity of poly(α-methyl styrene)capsules in microencapsulation process
下载PDF
导出
摘要 为实现对制备聚-α-甲基苯乙烯(PAMS)空心微球的乳液微封装过程中双重乳液固化速率的调控,实验测量了不同固化工艺条件下双重乳液中油相有机溶剂氟苯向外水相的扩散速率,研究了双重乳液固化速率对最终PAMS微球球形度的影响。结果表明,改变外水相中的氟苯浓度可以控制油相溶剂氟苯向外水相扩散的速率,从而改变双重乳液的固化速率。在双重乳液固化过程的关键阶段,通过降低氟苯扩散速率来延缓双重乳液的固化速率是提高最终PAMS微球球形度的有效途径。通过优化双重乳液的固化速率,单批次PAMS微球中球形偏离度值低于1μm的微球比例从1.9%提高到30.4%。 To study the influence of solidification rates of double emulsions on the sphericity of the resulting poly(α-methyl styrene)(PAMS)capsules in the microencapsulation process of PAMS capsules,the diffusion rates of fluorobenzene from oil phase to outer water phase under different conditions were experimentally measured,and the curing process of double emulsions under corresponding curing conditions were investigated.The results showed that the concentration of fluorobenzene in the outer water phase had a significant effect on the diffusion rate of fluorobenzene,which directly determined the solidification rate of double emulsions and then the sphericity of the resulting PAMS capsules.During the key phase of the solidification process of double emulsions,keeping proper concentrations of fluorobenzene in the outer water phase could remarkably reduce the solidification rate of double emulsions and consequently improve the sphericity of PAMS capsules.By optimizing the concentration of fluorobenzene in the outer water phase,the batch percentages of PAMS capsules with out-of-round less than 1 μm increased from 1.9% to 30.4%.
出处 《化工学报》 EI CAS CSCD 北大核心 2013年第7期2446-2452,共7页 CIESC Journal
基金 中国工程物理研究院科学技术发展基金项目(2010A0302015 2011B0302058)~~
关键词 微封装 双重乳液 PAMS 固化 microencapsulation double emulsions PAMS solidification
  • 相关文献

参考文献19

二级参考文献47

  • 1李波,陈素芬,张占文.内表面掺硅聚苯乙烯空心微球初步研究[J].强激光与粒子束,2004,16(8):1005-1008. 被引量:13
  • 2张林,崔保顺,周兰,袁玉萍.微封装法制备空心塑料微球[J].强激光与粒子束,1995,7(1):151-156. 被引量:16
  • 3亚当森AW 顾惕人(译).表面的物理化学[M].北京:科学出版社,1985.. 被引量:2
  • 4REGAN S P, DELETTREZ J A, JAANIMAGI P A, et al. Characterization of direct-driveimplosion core conditions on OMEGA with time resolved Ar K-shell spectroscopy, LLE review quarterly report [R]. Rochester: University of Rochester, 2001. 被引量:1
  • 5TAKAGI M, NORIMATSU T, YAMANAKA T, et al. Development of deuterated polystyrene shells for laser fusion by means of a density matched emulsion method[J]. Journal of Vacuum Science and Technology A, 1991, 9 (4): 2 145-2 148. 被引量:1
  • 6NORIMATSU T. Fabrication of vacuoles free polystyrene shells over a wide diameter range using a W/O/W emulsion method[J]. Journal of Moscow Physical Society, 1998, 8: 71-78. 被引量:1
  • 7LI Bo, ZHANG Zhanwen, WANG Changyang, et al. Preparation of polystyrene-poly(vinyl alcohol) double shell[J]. Proceedings of the SHE, 2003, 5 228:723 727. 被引量:1
  • 8DOKOU E, BARTEAU M A, NORMAN J, et al. Effect of gravity on colloidai deposition studied by atomic force microscopy[J]. Journal of Collid and Interface Science, 2001, 240:9 -16. 被引量:1
  • 9Letts S A, Fearon E M, Buckley S R, et al. Fabrication of polymer shells using a depolymerizable mandrel[J]. Fusion Technology, 1995, 28(5) : 1797-1801. 被引量:1
  • 10McQuillan B W, Nikroo A, Steinman D A, et al. The PAMS/GDP process for production of ICF target mandrel[J]. Fusion Technology, 1997, 31(4) :381-384. 被引量:1

共引文献40

同被引文献101

引证文献6

二级引证文献19

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部