摘要
锅炉管用钢15CrMoG(/%:0.12～0.18C、0.17～0.35Si、0.40～0.70Mn、≤0.015P、≤0.010S、0.80～1.10Cr、0.40～0.55Mo、≤0.08V、≤0.020Alt)要求非金属夹杂物的级别C≤1.0、Ds≤1.0。该钢的生产流程为铁水预处理-120 t LD-LF-RH-280 mm×380 mm连铸坯-轧制Φ100～Φ120 mm圆管坯。通过铁水深脱硫、LD终点控制0.03%～0.09%C、0.004%～0.012%P、0.006%～0.015%S,加铝铁2.5 kg/t的低铝脱氧,使用碱度为3～4的精炼渣,使中间包钢水的P含量为0.005%～0.012%,S含量0.005%～0.008%,Al含量为0.004%～0.008%,圆管坯的各项指标均满足用户协议要求。
The rating of inclusions in steel 15CrMoG for boiler tube （/% ： 0. 12 - 0. 18C, 0. 17 - 0. 35Si, O. 40 -0. 70Mn, ≤0. 01SP, ≤0. 010S, 0. 80 - 1.10Cr, 0. 40 -0. 55Mo, ≤0. 08V, ≤0. 020Alt） is that C series ≤1.0 and Ds series ≤ 1.0. The production flow sheet of the steel is hot metal pretreatment-120 t LD-LF-RH-280 mm× 380 mm bloom casting-rolling to Фl00-Фl20 mm round tube blank. With hot metal deepening desulphurization, LD end point controlling 0. 03% - 0. 09% C, 0. 004% - 0. 012% P, 0. 006% - 0. 015% S, low aluminium deoxidation with adding 2. 5 kg/t alumin- ium-iron, and using refining slag with basicity 3 -4, as a result in liquid steel in tundish the P content is 0. 005% -0. 012% , the S content is 0. 005% - 0. 008% and the aluminium content is 0. 004% - 0. 008% , and the each index of round tube blank all meet the reouirement of user terms of agreement.
出处
《特殊钢》
北大核心
2012年第5期32-34,共3页
Special Steel
关键词
电站
锅炉管用钢15CrMoG
磷
硫
铝
生产实践
Power Station, Steel 15CrMoG for Boiler Tube, P, S, Al, Production Practice