DM308玻璃对改善Pyrex玻璃在可伐合金表面开裂的影响 被引量:1

Effect of DM308 glass on cracking improving of Pyrex glass on the surface of Kovar alloy
下载PDF
导出
摘要 研究了在可伐合金与Pyrex玻璃之间引入DM308玻璃层对改善Pyrex玻璃在可伐合金表面开裂的影响。结果表明,采用涂覆的方法可以引入约200μm厚的DM308玻璃,而采用加热玻坯的方法可以引入较厚(2 mm)的DM308玻璃。在Pyrex玻璃和可伐合金之间引入DM308玻璃过渡层可以解决Pyrex玻璃开裂的问题,但是引入的DM308玻璃需要一定的厚度(约2 mm),而且在950℃下的热处理时间不得超过30 min。 The effect of DM308 glass layer between Pyrex glass and Kovar alloy on cracking improving of Pyrex glass on the surface of Kovar alloy was investigated. The results indicate that the thinner DM308 layer (about 200/μm) can be introduced by coating, and the thicker DM308 layer (2 mm) can be introduced by heating the DM308 billet. The problem of the cracking of Pyrex glass on the surface of Kovar alloy is solved by introducing DM308 glass as transition layer with certain thickness (about 2 ram), and the heat treatment time is controlled less than 30 min at 950℃.
出处 《电子元件与材料》 CAS CSCD 北大核心 2012年第4期45-48,共4页 Electronic Components And Materials
基金 深圳市科技局资助项目(No.JC201006020768A)
关键词 可伐合金 DM308玻璃 Pyrex玻璃 表面开裂 Kovar alloy DM308 glass Pyrex glass surface cracking
  • 相关文献

参考文献7

二级参考文献39

共引文献58

同被引文献3

  • 1TANAKA K,HIRAO K,SOGA N,et al.Preparation magnetic properties of glass-ceramics containing magnetite mi-crocrystals in calcium iron aluminoborate system[].Journal of Magnetism and Materials.1997 被引量:1
  • 2Wang Qian,Sun Hang,Cao Haifeng, etc.Porous glasses in the 21st century---a short review[].Journal Of Sichuan University (Engineering Science Edition).2002 被引量:1
  • 3曾华瑞,阮玉忠,于岩,刘慧颍.氟化钙晶核剂对废啤酒瓶微晶玻璃的影响[J].硅酸盐通报,2008,27(2):345-348. 被引量:10

引证文献1

二级引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部