射流电沉积镍中晶体形态的可控生长 被引量:1

Controllable growth of crystal morphology of Ni jet-electrodeposition
下载PDF
导出
摘要 利用分形理论编程模拟了射流电沉积中沉积几率较小时粒子簇的生长形貌。基于模拟的原理,利用摆动射流电沉积改变了枝晶的树枝状分形生长特性,制备不同电流密度、摆动速度、NiSO4浓度和电解液温度时的二维多孔交织的金属镍枝晶簇。结果表明:随着电流密度的增大,枝晶簇开始由分形生长形态向多孔交织形态转变,分形维数也随之增大。随着摆动速度的减小,枝晶簇向致密、均匀的多孔交织形态转变明显,分形维数逐渐增大。NiSO4浓度较小时,枝晶簇的分枝较多,形貌较为致密;NiSO4浓度最大时,气泡的析出量大大减少,枝晶簇的分枝显著减少,难以形成多孔交织的组织;分形维数随NiSO4浓度的变化先增大后减小;电解液温度的升高使枝晶簇的形貌向致密型转变,分形维数逐渐增大。 The dendrite growth at smaller depositing probability was simulated in jet-electrodeposition with fractal theory.Based on the simulation,by swinging jet-electrodeposition,the branch-like fractal growth of dendrite was altered,the porous interlaced dendrites at different current densities,swinging steps,NiSO4 concentrations and electrolyte temperatures were prepared.The results indicate that with increasing the current density,the morphology of dendrite becomes porous with an increased fractal dimension.With decreasing the swinging speed,the dendrite growth has an obvious change to dense and uniform structure,and the fractal dimension increases gradually.When the concentration of NiSO4 is small,the dendrite has an obvious dense and uniform structure with volumes of branches.When the concentration of NiSO4 is the highest,a decrease of the H2 bubbles number leads to a large decrease of the branches number,and thus the porous interlaced dendrite cannot be prepared at this moment.The fractal dimension begins to increase and then decrease with the concentration of NiSO4 increasing.As the temperature of the electrolyte increases,the dendrite growth has a change to dense structure with the fractal dimension increasing.
出处 《中国有色金属学报》 EI CAS CSCD 北大核心 2011年第11期2903-2908,共6页 The Chinese Journal of Nonferrous Metals
基金 国家自然科学基金资助项目(50575104) 江苏省自然科学基金资助项目(BK2009375) 南京航空航天大学基本科研专项资助项目(NS2010135)
关键词 枝晶 射流电沉积 分形 Ni dendrite jet-electrodeposition fractal
  • 相关文献

参考文献15

  • 1SAWADA Y, DOUGHERTY A, GOLLUB J R Dendritic and fractal patterns in electrolytic metal deposits[J]. Phys Rev Lett, 1986, 56(12): 1260-1263. 被引量:1
  • 2MATSUSHITA M, SANO M, HAYAKAWA Y, HONJO H, SAWADA Y. Fractal structures of zinc metal leaves grown by electrodeposition[J]. Phys Rev Lett, 1984, 53(3): 286-289. 被引量:1
  • 3MOGI I, OKUBO S, NAKAGAWA Y. Dense radical growth of silver metal leaves in a high magnetic field[J]. J Phys Soc Jpn, 1991, 60: 3200-3202. 被引量:1
  • 4尤红军,方吉祥,孔鹏,丁秉钧.扩散限制和非扩散限制对电沉积银形貌的影响[J].稀有金属材料与工程,2008,37(6):1042-1045. 被引量:6
  • 5BRADY R M, BALL R C. Fractal growth of copper electrodeposits[J]. Nature, 1984, 309(5): 225-229. 被引量:1
  • 6HILL S C, ALEXANDER J I D. Modified diffusion-limited aggregation simulations of electrodeposition in two dimensions[J]. Phys Rev E, 1997, 56: 4317-4327. 被引量:1
  • 7王桂峰,黄因慧,田宗军,刘志东,陈劲松,高雪松.平行板电极喷射电沉积中的枝晶分形生长[J].华南理工大学学报(自然科学版),2008,36(4):35-39. 被引量:12
  • 8陈书荣,谢刚,崔衡,马文会.金属铜电沉积过程中分形研究[J].中国有色金属学报,2002,12(4):846-850. 被引量:29
  • 9GRIER D BEN-JACOB E, CLARKE R, SANDER L M. Morphology and microstructure in electrochemical deposition of zinc[J]. Phys Rev Lett, 1986, 56(12): 1264-1267. 被引量:1
  • 10CHAO-PENG C, JORNE J. Fractal analysis of zinc electrodeposition[J]. J Electrochem Soc, 1990, 137(7): 2047-2051. 被引量:1

二级参考文献42

共引文献59

同被引文献13

  • 1CHEN Jin-song. Microstructure and performance of nanocrystalline nickel parts[J]. Advanced Materials Research, 2011,287/290: 420-423. 被引量:1
  • 2KARNIK M, GHOSH A, SHEKHAR R. Fused deposition process combining electrochemical discharge with high speed selective jet electrodeposition[J]. Transactions of the Institute of Metal Finishing, 2009, 87(5): 264-271. 被引量:1
  • 3BEN-JACOB E, GARIK E The formation of patterns in non-equilibrium growth [J]. Nature, 1990, 343: 523-530. 被引量:1
  • 4BOCKING C, CAMERON B. Use of high speed selective jet electrodeposition of gold for the plating of connectors[J]. Transactions of the Institute of Metal Finishing, 1994, 72(1): 33-40. 被引量:1
  • 5KUNIEDA M, KATOH R, MORI Y. Rapid prototying by selective electrodeposition using electrolyte jet[J]. CIRP Annals-Manufacturing Technology, 1998, 47(1): 161-164. 被引量:1
  • 6KOZHANOV V N, SMIRNOV B N, FILOSOFOVA A B, PUTILINA O V. Variation of the surface morphology of a copper eleetrodeposit during its growth. I. Formation of dendritic structure[J]. Powder Metallurgy and Metal Ceramics, 1988, 27(7): 512-517. 被引量:1
  • 7THOMPSON P, COX D E, HASTINGS J B. Rietveld refinement of Debye-Scherrer synchrotron X-ray data from Al2O3[J]. Journal of Applied Crystallography, 1987, 20(2): 79-83. 被引量:1
  • 8CHEN Ming-wei, MA En, HEMKER K J, SHENG Hong-wei, WANG Yin-min, CHENG Xue-mei. Deformation twinning in nanocrystalline aluminum[J]. Science, 2003, 300(5623): 1275-1277. 被引量:1
  • 9GRIFFITHS D J. Introduction to electrodynamics[M]. New Jersey: Addison Wesley, 1999: 301-304. 被引量:1
  • 10李学磊,朱增伟,朱荻.游离粒子辅助磨对镍锰合金电铸层表面质量及锰含量的影响[J].材料工程,2010,38(12):14-18. 被引量:3

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部