The recrystallization texture in commercially pure Al is investigated after the samples are rolled differently and annealed.The samples with low rol- ling reductions could be generally recovered or recrystallized in situ and characterized by the re- tained G{110}<001>component.This recovery process decreases during annealing with the increase of reduction.The appearance of the B/R{359}. <132>and R{123}<634>components de- pending on the rolling reduction is investigated and the less developed Cube{100}<001>component in commercially pure ahninium is also discussed.
The recrystallization texture in commercially pure Al is investigated after the samples are rolled differently and annealed.The samples with low rol- ling reductions could be generally recovered or recrystallized in situ and characterized by the re- tained G{110}<001>component.This recovery process decreases during annealing with the increase of reduction.The appearance of the B/R{359}. <132>and R{123}<634>components de- pending on the rolling reduction is investigated and the less developed Cube{100}<001>component in commercially pure ahninium is also discussed.