Adsorption behavior of ytterbium (Ⅲ) on gel-type weak acid resin 被引量:3

Adsorption behavior of ytterbium (Ⅲ) on gel-type weak acid resin
原文传递
导出
摘要 The adsorption and desorption behaviors of Yb(Ⅲ) on gel-type weak acid resin (110) were investigated. The influence of operational conditions such as contact time,initial concentration of Yb(Ⅲ),initial pH of solution and temperature on the adsorption of Yb(Ⅲ) were also examined. The results showed that the optimal adsorption condition of 110 resin for Yb(Ⅲ) was achieved at pH=5.5 in HAc-NaAc medium. The maximum uptake capacity of Yb(Ⅲ) was 265.8 mg/g at 298 K. Yb(Ⅲ) could be eluted by using 3.0 mol/L HCl solution and the 110 resin could be regenerated and reused. The adsorption of Yb(Ⅲ) followed the Langmuir isotherm,and the correlation coefficients were evaluated. Various thermodynamic parameters such as standard enthalpy change (△H),standard entropy change (△S) and standard free energy change (△G) were evaluated. The adsorption of Yb(III) on the 110 resin was found to be endothermic in nature. Thomas model was successfully applied to experimental data to predict the breakthrough curves and to determine the characteristics parameters of the column useful for process design. And the resin sample both before and after adsorption was described by IR spectroscopy. The adsorption and desorption behaviors of Yb(Ⅲ) on gel-type weak acid resin (110) were investigated. The influence of operational conditions such as contact time,initial concentration of Yb(Ⅲ),initial pH of solution and temperature on the adsorption of Yb(Ⅲ) were also examined. The results showed that the optimal adsorption condition of 110 resin for Yb(Ⅲ) was achieved at pH=5.5 in HAc-NaAc medium. The maximum uptake capacity of Yb(Ⅲ) was 265.8 mg/g at 298 K. Yb(Ⅲ) could be eluted by using 3.0 mol/L HCl solution and the 110 resin could be regenerated and reused. The adsorption of Yb(Ⅲ) followed the Langmuir isotherm,and the correlation coefficients were evaluated. Various thermodynamic parameters such as standard enthalpy change (△H),standard entropy change (△S) and standard free energy change (△G) were evaluated. The adsorption of Yb(III) on the 110 resin was found to be endothermic in nature. Thomas model was successfully applied to experimental data to predict the breakthrough curves and to determine the characteristics parameters of the column useful for process design. And the resin sample both before and after adsorption was described by IR spectroscopy.
出处 《Journal of Rare Earths》 SCIE EI CAS CSCD 2011年第5期407-412,共6页 稀土学报(英文版)
基金 Project supported by the grants from the National Key Technologies Research and Development Program of China (2008BAD94B09) the Key Grant of Education Department of Zhejiang Province, China (Z200907459)
关键词 gel-type weak acid resin (110 resin) ytterbium(Ⅲ) ADSORPTION PARAMETER Thomas model rare earths gel-type weak acid resin (110 resin) ytterbium(Ⅲ) adsorption parameter Thomas model rare earths
  • 相关文献

参考文献26

二级参考文献79

共引文献23

同被引文献20

引证文献3

二级引证文献36

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部