The temperature dependence of carrier transport properties of Alx Gal-xN/InyGal-yN/CaN and AlzGal-xN/GaN heterostructures has been investigated. It is shown that the Hall mobility in Alo.25Gao.75N/Ino.03Gao.97N/GaN heterostructures is higher than that in Alo.25Gao.75N/GaN heterostructures at temperatures above 500 K, even the mobility in the former is much lower than that in the latter at 300 K. More importantly, the electron sheet density in Alo.25Gao.75N/Ino.03Gao.97N/GaN heterostructures decreases slightly, whereas the electron sheet density in Al0.25Gao.75N/CaN heterostructures gradually increases with increasing temperature above 500 K. It is believed that an electron depletion layer is formed due to the negative polarization charges at the Iny Can-yN/GaN heterointerface induced by the compressive strain in the InyCal-yN channel, which effectively suppresses the parallel conductivity originating from the thermal excitation in the underlying GaN layer at high temperatures.
The temperature dependence of carrier transport properties of Alx Gal-xN/InyGal-yN/CaN and AlzGal-xN/GaN heterostructures has been investigated. It is shown that the Hall mobility in Alo.25Gao.75N/Ino.03Gao.97N/GaN heterostructures is higher than that in Alo.25Gao.75N/GaN heterostructures at temperatures above 500 K, even the mobility in the former is much lower than that in the latter at 300 K. More importantly, the electron sheet density in Alo.25Gao.75N/Ino.03Gao.97N/GaN heterostructures decreases slightly, whereas the electron sheet density in Al0.25Gao.75N/CaN heterostructures gradually increases with increasing temperature above 500 K. It is believed that an electron depletion layer is formed due to the negative polarization charges at the Iny Can-yN/GaN heterointerface induced by the compressive strain in the InyCal-yN channel, which effectively suppresses the parallel conductivity originating from the thermal excitation in the underlying GaN layer at high temperatures.
基金
Project supported by the National Natural Science Foundation of China (Grant Nos.60906041,60736033,60890193,and 10774001)