摘要
采用真空扩散连接技术对GH4169合金进行了焊接,分析了GH4169合金接头界面结构及扩散连接工艺参数对界面扩散孔隙及接头力学性能的影响.结果表明,GH4169直接扩散连接,在连接温度为950~1 150℃的范围内,随着温度的升高,连接时间的延长和连接压力的增大,界面的扩散孔隙数目逐渐减少,尺寸逐渐变小,接头抗拉强度达到658 MPa,但接头依旧有不连续的孔洞存在.采用铜中间层进行GH4169的扩散连接时,在界面处有固溶体层生成,接头抗拉强度得到明显的提高,最高可达745MPa.
The vacuum diffusion bonding process was used to weld GH4169 alloy and the effects of process parameters on the interface structure,interface bonding holes and mechanical properties of the joints were investigated.The experimental results without interlayer show that with the increase of diffusion time and diffusion pressure in the range of 950-1 150 ℃,both the number and size of interface bonding hole decrease and the maximum tensile strength is 658 MPa,but the discontinuous interface holes still exist.With the Cu interlayer,the solid solution layer exists on the interface and the maximum tensile strength is 745 MPa.
出处
《焊接学报》
EI
CAS
CSCD
北大核心
2010年第11期13-16,共4页
Transactions of The China Welding Institution
基金
哈尔滨工业大学优秀团队计划资助项目
关键词
镍基高温合金
扩散连接
中间层
抗拉强度
nickel-base alloy
diffusion bonding
interlayer
tensile strength