摘要
Effects of the content of Dy on structure and magnetic properties of DyxFe60.5-xPt39.5 alloys（x = 0, 0.5, 1.0, 1.5） were investigated. The results of XRD analysis proved that the phase-transitional temperature of DyxFe60.5-xPt39.5 alloys from disordered face-centered-cubic structure to ordered face-centered-tetragonal cubic structure decreases with the increase of the content of Dy（x）. Suitable content of Dy can improve the exchange coupling between soft magnetic phase and hard magnetic phase by refining grain size, while the remanence ratio and coercivity of the Fe60.5Pt39.5 alloy can be significantly improved by a small replacement of Fe by Dy, good magnetic properties were obtained in Dy0.5Fe60.0Pt39.5 alloys.
Effects of the content of Dy on structure and magnetic properties of DyxFe60.5-xPt39.5 alloys（x = 0, 0.5, 1.0, 1.5） were investigated. The results of XRD analysis proved that the phase-transitional temperature of DyxFe60.5-xPt39.5 alloys from disordered face-centered-cubic structure to ordered face-centered-tetragonal cubic structure decreases with the increase of the content of Dy（x）. Suitable content of Dy can improve the exchange coupling between soft magnetic phase and hard magnetic phase by refining grain size, while the remanence ratio and coercivity of the Fe60.5Pt39.5 alloy can be significantly improved by a small replacement of Fe by Dy, good magnetic properties were obtained in Dy0.5Fe60.0Pt39.5 alloys.
基金
Funded by the National Natural Science Foundation of China(No.50261002&50661002)